Temperature dependence of electric resistance and magnetoresistance of pressed nanocomposites of multilayer nanotubes with the structure of nested cones

V. I. Tsebro,O. E. Omel'yanovskii,E. F. Kukovitskii,N. A. Sainov,N. A. Kiselev,D. N. Zakharov

DOI: https://doi.org/10.1134/1.558593

1998-12-24

Abstract:Bulk samples of carbon multilayer nanotubes with the structure of nested cones (fishbone structure) suitable for transport measurements, were prepared by compressing under high pressure (~25 kbar) a nanotube precursor synthesized through thermal decomposition of polyethylene catalyzed by nickel. The structure of the initial nanotube material was studied using high-resolution transmission electron microscopy. In the low-temperature range (4.2 - 100 K) the electric resistance of the samples changes according to the law ln \rho ~ (T_0/T)^{1/3}, where T_0 ~ 7 K. The measured magnetoresistance is quadratic in the magnetic field and linear in the reciprocal temperature. The measurements have been interpreted in terms of two-dimensional variable-range hopping conductivity. It is suggested that the space between the inside and outside walls of nanotubes acts as a two-dimensional conducting medium. Estimates suggest a high value of the density of electron states at the Fermi level of about 5 10^{21} eV^{-1} cm^{-3}.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the electrical transport properties and magnetoresistance characteristics of multi - walled carbon nanotubes (with nested conical structures, i.e., fish - bone structures) at low temperatures. Specifically, the researchers focus on the following points:

1. **Material Preparation and Structural Characterization**:
- Bulk samples suitable for transport measurements were prepared by high - pressure compression (about 25 kbar) of nanotube precursors synthesized by nickel - catalyzed pyrolysis of polyethylene.
- The structure of the initial nanotube material was studied using high - resolution transmission electron microscopy (HRTEM).

2. **Variation Law of Resistance with Temperature**:
- In the low - temperature range (4.2–100 K), the resistance change of the sample follows the formula:
\[
\ln \rho \propto \left(\frac{T_0}{T}\right)^{1/3}
\]
where \( T_0\approx7 \, \text{K} \).

3. **Magnetoresistance Characteristics**:
- The measured magnetoresistance is expressed as a quadratic function of the magnetic field and a linear function of the reciprocal of the temperature.
- These characteristics are interpreted as the result of two - dimensional variable - range hopping conductivity.

4. **Estimation of Electron Density of States**:
- Based on the above experimental results, the two - dimensional electron density of states \( g^*(\mu) \) and the three - dimensional electron density of states \( g(\mu) \) near the Fermi level were estimated as follows:
\[
g^*(\mu) \sim 7.5\times 10^{15} \, \text{eV}^{-1} \text{cm}^{-2}
\]
\[
g(\mu) \sim 5\times 10^{21} \, \text{eV}^{-1} \text{cm}^{-3}
\]

5. **Theoretical Explanation and Comparison**:
- These results were compared with previous studies on single - walled or multi - walled carbon nanotubes, and it was found that these materials exhibit similar conductive behaviors at low temperatures, indicating that they have a very high electron density of states near the Fermi level, similar to metals.

In summary, this paper aims to gain an in - depth understanding of the electrical transport mechanism of multi - walled carbon nanotubes with nested conical structures at low temperatures and explore their possible practical application prospects.