Abstract:The effect of porosity in composite materials has been studied for years due to its deleterious effects on mechanical properties, especially matrix dominated properties. Currently there is an increasing use of composites in infrastructure worldwide, for example bridge components, residential and building structures, marine structures such as piers and docks, and large industrial chemical tanks. Most of these applications use fiberglass composites. Unfortunately, most of the published literature has focused on carbon fiber composites, in which fiber diameter and gas-fiber interactions are different than fiberglass composites. Therefore, the present study was undertaken to revisit the effect of porosity but specifically in fiberglass composites. The goal of this experimental study was to implement and evaluate various methods for creating porosity in fiberglass composites in a controlled manner in terms of obtaining repeatable void content, morphology, and location within the laminate. The various methods included using different amounts of autoclave pressure, adding a small amount of water between prepreg layers, and using dry fabric layers to starve the laminate of resin. Ultrasonic C-scan nondestructive evaluation was used to assess the quality of the cured panels, as well as optical and electron microscopy and void content measurements via resin burn-out. The cured panels were mechanically tested using the short beam shear (SBS) method. The results showed that the water spray method proved to be the best in terms of producing noticeably different levels of porosity, although the panels required drying to remove residual water after cure. The voids from all three techniques were either oval or elongated in-plane between the plies, but they were not uniformly distributed in-plane. The use of C-scan proved to be helpful for characterizing overall uniformity of each panel, although the results could not be used to directly compare void content between panels. The use of SBS testing was successful for evaluating void dominated properties in panels with high void content, although it was not very sensitive to coupons with lower void contents. Several interesting observations are offered in this manuscript of the fracture surface details and their relation to the SBS load deflection curves. Overall, it was found that the failure mechanisms were mixed mode and the voids did not serve as failure initiation sites. However, the voids participated mainly in the horizontal propagation of cracks between layers, presumably making it easier when they were intersected by a crack and reducing SBS strength.

Internal characteristics analysis of woven/unidirectional composite angle part by VBO process

Complex angle part fabricated by vacuum bag only process with interleaved dry fiber and prepreg

Design and analysis of the mandrel structure for a composite S-shaped inlet

An Algorithm for Automatically Establishing a Multi- Parameter RVE Model for Z-Pin Composite Laminates

Modeling on the Effect of Automated Fiber Placement Induced Gaps in Curved Composite Laminates

Analysis of in-plane compression failure mechanism in carbon fiber braided composite with different off-axial angles

Effects of Lateral Space and Angle of Attack on Ventilated Partial Cavity

Experimental Analysis of Pre-Forming Parameters on Abnormalities, Thickness, and Void Content of Glass/Epoxy Composite In VBO-Oven Cure Manufacturing

Experimental Investigation of Z-pin Insertion Angles on the Mechanical Behavior and Failure Mechanism of Compression after Impact for CFRP Laminates

Process parameters optimization of double‐vacuum‐bag technology for carbon fiber/resin composites

Experimental Method to Determine the Draping Behavior of Auxiliary Materials for the Vacuum Bagging of CFRP Parts on Doubled-Curved Surfaces

Buckling analysis of laminated composite plates with variable fibre orientation angle

Simulation analysis of parametric effects on consolidation ofangle bended composites

Mechanical Simulation of Thermoplastic Composite Fiber Variable-Angle Laminates

Mechanical Properties of Thermoplastic Variable-Angle Composite Laminations for Conical Shells

Investigation of various techniques for controlled void formation in fiberglass/epoxy composites

Contrastive Analysis of Pores for the CFRP Laminates and Corner of L-Shape CFRP Components

Effect of multi‐angle lamination on mechanical properties and damages behavior of carbon fiber reinforced resin matrix composites

Optimization of Fiber Orientation and Topology for Curved-Folded Laminated Bamboo Veneer Shells

Automated Fiber Placement Path Planning and Analysis of Pressure Vessels

Microstructure, hygrothermal, and mechanical properties of interlaminar toughening of CFRP composite using polyamide veil