Understanding How Anion Exchange Membranes and Cationic Polymer/Catalyst Interactions Behave with Time in Alkaline Electrolysis

Andrew M. Herring,Mei-Chen Kuo,Ivy Wu,Jack Creel,Marco Salgado,E. Bryan Coughlin

DOI: https://doi.org/10.1149/ma2023-02391895mtgabs

2023-12-22

ECS Meeting Abstracts

Abstract:We are leveraging our existing success with anion exchange membranes (AEM) to develop new highly stable and highly conductive membranes and ionomers for AEM electrolysis. Our novel and scalable tri-block co-polymers ABA or BAB, where the A block can be functionalized with an advanced chemically stable cation and the B block is an unsaturated polymer that when hydrogenated results in high anion conduction membranes with exceptional mechanical strength and durability analogous to polyethylene (PE). We have also developed a novel immobilization technology for processable catalyst inks. Synergistically the A and B block lengths and chemistries are tuned to achieve all the properties desirable for an anion exchange membrane for electrolyzer applications. Random polymers of the same A and B chemistries can also be formulated for additional fidelity in chemically compatible ionomers for the membrane electrode assemblies (MEA). These systems are unique in that they achieve very high dissociation of anions beyond OH - , giving CO 3 2- σ60°C and 25 cm 2 cells. We have begun to understand the science behind ionomer catalyst interactions and initially used a commercial Ag nano-catalyst as a model system. Few ave studied the effect of ionomer chemistry and catalyst or catalyst type and loadings on performance. We have shown durability of > 600 h at 0.5 A cm -2 and continue to see improvements. It should be noted that the voltage is dropping in theses tests, at end of test at –ve 60 μV h -1 is achieved, while this may be interpreted as evidence of membrane thinning when the cell was dissembled the membrane thickness was ca. the same as at the beginning of test (80 μm), indicating slow, but long term conditioning, the cell did not reach the point at which a +ve degradation rate was observed. Further investigation of cell conditioning indicated that these cells currently take 40-50 hs under load to reach steady state operation (this break in time will be understood and significantly shortened) giving 400MV improvement at 1 A cm -2 . With a MnO 2 catalyst the voltage at 0.5 A cm -2 drops to 1.5 V indicating that the target of 2 A cm -2 at 1.8 V will be easily achieved with further investigation.