Ultrahigh energy density in short-range tilted NBT-based lead-free multilayer ceramic capacitors by nanodomain percolation
Hongfen Ji,Dawei Wang,Weichao Bao,Zhilun Lu,Ge Wang,Huijing Yang,Ali Mostaed,Linhao Li,Antonio Feteira,Shikuan Sun,Fangfang Xu,Dejun Li,Chao-Jie Ma,Shi-Yu Liu,Ian M. Reaney
DOI: https://doi.org/10.1016/j.ensm.2021.01.023
IF: 20.4
2021-06-01
Energy Storage Materials
Abstract:<p>Dense pseudocubic 0.62Na<sub>0.5</sub>Bi<sub>0.5</sub>TiO<sub>3</sub>-0.3Sr<sub>0.7</sub>Bi<sub>0.2</sub>TiO<sub>3</sub>-0.08BiMg<sub>2/3</sub>Nb<sub>1/3</sub>O<sub>3</sub> (NBT-SBT-0.08BMN) ceramics with excellent recoverable energy density, <em>W<sub>rec</sub></em> = 7.5 J/cm<sup>3</sup>, and conversion efficiency, <em>η</em> = 92%, were synthesized. Large electric breakdown strength was facilitated by electrical homogeneity, high resistivity and large activation energy (1.86 eV). Transmission electron microscopy identified the presence of polar nano-regions (PNRs) in a matrix of short coherence in-phase and antiphase octahedral tilting. Combining polar and tilt order restricted the crystal classes of PNRs to tetragonal, orthorhombic and monoclinic. Using these symmetries, the enhancement of polarization was explained using Landau-Devonshire phenomenology and percolation theory. Octahedral tilting and introduction of larger B-site ions (Mg<sup>2+</sup>, Nb<sup>5+</sup>) inhibited long range polar coupling, minimizing strain and maximizing <em>η. W<sub>rec</sub></em> was further improved to 18 J/cm<sup>3</sup> (>1000 kV/cm) in multilayers whose properties were stable from 0.01–100 Hz, from 20°C–160°C and up to 10<sup>6</sup> cycles, attractive for pulsed power applications and power electronics.</p>
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology