Synergy of a Stabilized Antiferroelectric Phase and Domain Engineering Boosting the Energy Storage Performance of NaNbO 3 -Based Relaxor Antiferroelectric Ceramics
Jikang Liu,Peng Li,Chongyang Li,Wangfeng Bai,Shiting Wu,Peng Zheng,Jingji Zhang,Jiwei Zhai
DOI: https://doi.org/10.1021/acsami.2c01507
2022-04-07
Abstract:Relaxor antiferroelectric (AFE) ceramic capacitors have drawn growing attention in future advanced pulsed power devices for their superior energy storage performance. However, state of the art dielectric materials are restricted by desirable comprehensive energy-storage features, which have become a longstanding hurdle for actual capacitor applications. Here, we report that a large energy density Wrec of 5.52 J/cm3, high efficiency η of 83.3% at 560 kV/cm, high power density PD of 114.8 MW/cm3, ultrafast discharge rate t0.9 of 45 ns, and remarkable stability against temperature (30–140 °C)/frequency (5–200 Hz)/cycles (1–105) are simultaneously achieved in 0.7 NaNbO3-0.3 CaTiO3 relaxor AFE ceramics via the synergy of stabilized AFE R phase and domain engineering in combination with breakdown strength enhancement. The structural origin for these achievements is disclosed by probing the in situ microstructure evolution by means of the first-order reversal curve method, piezoelectric force microscopy, and Raman spectroscopy. The highly dynamic polar nanoregions and stabilized AFE R phase synergistically generate a linear-like and highly stable polarization field response over a wide temperature and field scope with concurrently improved energy density and efficiency. This work offers a new solution for designing high-performance next-generation pulsed power capacitors.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c01507.Experimental section, dielectric properties, impedance spectroscopy, and unipolar P–E loops for (1 – x)NN-xCT ceramics at various temperatures, frequencies, cycle numbers and electric fields, SEM, UV–vis reflection spectrum, and XPS spectrum for the 0.7NN-0.3CT ceramic, PFM and Raman patterns at different temperatures, voltages, and times of the 0.7NN-0.3CT ceramic, and charge–discharge curves as functions of temperature, electric field, and cycle numbers for the 0.7NN-0.3CT ceramic (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology