Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

Prediction of hydrogen-assisted fracture under coexistence of hydrogen-enhanced plasticity and decohesion

Analysis of Hydrogen-Assisted Brittle Fracture Using Phase-Field Damage Modelling Considering Hydrogen Enhanced Decohesion Mechanism

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel

A predictive model unifying hydrogen enhanced plasticity and decohesion

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

A Coupled Cohesive Modeling Approach for Predicting Fractures in Low Alloy Steel under High-Pressure Hydrogen Gas

Hydrogen-Assisted Brittle Fracture Behavior of Low Alloy 30CrMo Steel Based on the Combination of Experimental and Numerical Analyses

Fracture Strain Model for Hydrogen Embrittlement Based on Hydrogen Enhanced Localized Plasticity Mechanism

Predictive Environmental Hydrogen Embrittlement on Fracture Toughness of Commercial Ferritic Steels with Hydrogen-Modified Fracture Strain Model

Cohesive Zone Modeling of Hydrogen-Induced Delayed Intergranular Fracture in High Strength Steels

NUMERICAL SIMULATION OF HYDROGEN INDUCED DELAYED FRACTURE OF AISI4135 HIGH STRENGTH STEEL USING COHESIVE ZONE MODELING

Prediction on Initiation of Hydrogen-Induced Delayed Cracking in High-Strength Steel Based on Cohesive Zone Modeling

Effect of Multiple Hydrogen Embrittlement Mechanisms on Crack Propagation Behavior of FCC Metals: Competition Vs. Synergy

A phase field model for elastic-gradient-plastic solids undergoing hydrogen embrittlement

Interaction Between Dislocations, Precipitates and Hydrogen Atoms in a 2000 MPa Grade Hot-Stamped Steel

A mechanism-based multi-trap phase field model for hydrogen assisted fracture

Embrittlement of Notched Duplex Stainless Steel: Role of Hydrogen-Assisted Void Growth and Cleavage

Hydrogen diffusion behavior within microstructures near crack tip: A crystal plasticity study

Computational predictions of hydrogen-assisted fatigue crack growth

Computational modelling of hydrogen assisted fracture in polycrystalline materials