Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Structure and properties of wet modified titanium dioxide with silane coupling agent KH-570

Studies on Preparation of KH - 570 Modified Nano - Titanium Dioxide and Its Dispersibility

Surface Organic Modification of SiO2 ＆ Al2O3 Coated TiO2 Particles with Titanate Coupling Reagent

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Organic Modification On The Sub-Micron Particles Of Tio2 Pre-Coated With Sio2 And Al2o3

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Preparation and characterization of nano-sized KH-570 modified titanium dioxide by sol-gel method

Hydrophobic modification and characterization of titanium dioxide

Surface Modification of Titanium Dioxide and Photocatalytic Activity of Its Coating Film

Preparation and Characterization of Silica-modified Titanium Dioxide Nanoparticles by Co-precipitation Method

Surface modification of nanometer titanium dioxide

Preparation and Characterization of Silanized Tio2 Nanoparticles and Their Application in Toner

Organic modification of ultrafine particles using carbon dioxide as the solvent

Modification of Titanium Dioxide Nanoparticles with 3-(Trimethoxysilyl)propyl Methacrylate Silane Coupling Agent

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

The synthesis of hydrophobic nano-TiO2 powder and its photocatalytic property

A Study on Surface Modification of Nano-scale TiO2 by Hexadecanoic Acid

Synthesis studies of sputtering TiO2 films on poly(dimethylsiloxane) for surface modification

Surface characteristics of hydrous silica-coated TiO2 particles

Preparation, Modification and Property Characterization of Nano-TiO2

Surface Organic Modification of Tio2 Powder and Relevant Characterization