Solution-Processed Quasi-Two-Dimensional/Nanoscrystals Perovskite Composite Film Enhances the Efficiency and Stability of Perovskite Light-Emitting Diodes
Pengfei Xia,Yao Lu,Yongzhe Li,Wenzhu Zhang,Wei Shen,Jie Qian,Ya’nan Wu,Wenjing Zhu,Hongtao Yu,Lihui Liu,Lingling Deng,Shufen Chen
DOI: https://doi.org/10.1021/acsami.0c07547
2020-08-20
Abstract:Solution-processed quasi-two-dimensional (Q-2D)/colloidal perovskite nanocrystals (PNCs) perovskite composite films are first prepared as the emitting layers of perovskite light-emitting diodes (PeLEDs). The subsequent multi-spin-coating of PNCs not only fills the gully-like fluctuations of the nanocrystal pinning-prepared Q-2D perovskite films and decreases their surface roughness but also transforms the bilayer perovskite nanosheets into multilayer ones, thus improving the charge transport and reducing the hole-injection barrier in the composite films. More importantly, the bromide vacancies and Pb defects in the Q-2D perovskites are removed via Br<sup>–</sup> supply and Pb-OOC-R interaction, in which the Br ions and COO<sup>–</sup> groups (from oleic acid) come from the PNC solution, and the radiation recombination is significantly enhanced. Based on the Q-2D/PNCs perovskite composite emitter, the PeLEDs achieve a maximum luminescence of ∼2.0 × 10<sup>4</sup> cd/m<sup>2</sup> and a peak current efficiency of 27.5 cd/A, showing 175 and 337% enhancements compared to the control device with the pristine Q-2D perovskite emitter. The lifetime for the luminance decaying to 50% of the initial intensity increases by a factor of 13.8, demonstrating that the device stability is also improved by the Q-2D/PNCs perovskite composite film.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c07547?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c07547</a>.Calculation of lattice constant and PL lifetime, supplementary experiment of ion-exchange-mediated self-assembly, experimental details; photographs of colloidal PNCs solution under ambient and UV light illumination (Figure S1); photographs of (a) pristine Q-2D and (b–e) Q-2D/PNCs*1, 3, 5 and 7 composite films (Figure S2); Q-2D and PNCs PL spectra of (a) Q-2D/PNCs*1, (b) Q-2D/PNCs*3, and (c) Q-2D/PNCs*5 films (Figure S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c07547/suppl_file/am0c07547_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology