Abstract:Bisphenol A dicyanate (BADCy) resin microparticles were prepared by precipitation polymerization synthesis and were homogeneously dispersed in a BADCy prepolymer matrix to prepare a BADCy self-reinforced composites. The active functional groups of the BADCy resin microparticles were characterized by Fourier transform infrared (FT-IR) spectroscopy. The results of an FT-IR curve showed that the BADCy resin microparticles had a triazine ring functional group and also had an active reactive group -OCN, which can initiate a reaction with the matrix. The structure of the BADCy resin microparticles was characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). From the TEM results, the BADCy resin microparticles dispersed in the solvent were nano-sized and distributed at 40-60 nm. However, from the SEM results, agglomeration occurred after drying, the BADCy resin particels were micron-sized and distributed between 0.3 μm and 0.6 μm. The BADCy resin prepolymer was synthesized in our laboratory. A BADCy self-reinforced composite was prepared by using BADCy resin microparticles as a reinforcement phase. This corresponds to a composite in which the matrix and reinforcement phase are made from different morphologies of the same monomer. The DSC curve showed that the heat flow of the microparticles is different from the matrix during the curing reaction, this means the cured materials should be a microscopic two-phase structure. The added BADCy resin microparticles as reaction sites induced the formation of a more complete and regular cured polymer structure, optimizing the cross-linked network as well as increasing the interplay between the BADCy resin microparticles and prepolymer matrix. Relative to the neat BADCy resin material, the tensile strength, flexural strength, compressive strength and impact strength increased by 98.1%, 40.2%, 27.4%, and 85.4%, respectively. A particle toughening mechanism can be used to explain the improvement of toughness. The reduction in the dielectric constant showed that the cross-linked network of the self-reinforced composite was more symmetrical and less polar than the neat resin material, which supports the enhanced mechanical properties of the self-reinforced composite. In addition, the thermal behavior of the self-reinforced composite was characterized by thermogravimetric analysis (TGA) and dynamic mechanical thermal analysis (DMTA). The results of DMTA also establishes a basis for enhancing mechanical properties of the self-reinforced composite.

Design of high-performance resin by tuning cross-linked network topology to improve CF/bismaleimide composite compressive properties

Cure of Neat Resins and Properties of Composites for Interpenetrating Polymer Networks from the Novel Bismaleimide and Cyanate Containing Naphthalene

A Novel Method for Through-Thickness Reinforcement of Laminated Composites Using Discrete Micro-Polarization-induced Fiber Injection (DMFI) Approach

Preparation and Characterization of Bismaleimide-Resin-Based Composite Materials

Molecular mechanics-based design of high-modulus epoxy to enhance composite compressive properties

Optimization and preparation of an allyl phenoxy-modified bismaleimide resin

The rigid-flexible balanced molecular crosslinking network transition interface: An effective strategy for improving the performance of bamboo fibers/poly(butadiene succinate-co-butadiene adipate) biocomposites

Utilizing in-situ construction of tailored block copolymer nanostructures to enhance CF/epoxy composites compressive properties

Enhancing interfacial performance of epoxy resin composites via in-situ nucleophilic addition polymerization modification of carbon fibers with hyperbranched polyimidazole

Establishing interphase with "rigid-flexible coupling" crosslinking network by supramolecular structure to improve interfacial properties of high modulus carbon fiber reinforced polymer composites

Constructing a multiscale rigid-flexible interfacial structure at the interphase by hydrogen bonding to improve the interfacial performance of high modulus carbon fiber reinforced polymer composites

Understanding compressive strength improvement of high modulus carbon-fiber reinforced polymeric composites through fiber-matrix interface characterization

Understanding of the Modified Bismaleimide Composite with Multifunctional Phthalonitrile and Its Outstanding Mechanical Properties

Simultaneously reducing the modulus difference and smoothing the modulus transition through bi-directional structural design for enhancing interfacial properties of carbon fiber/epoxy composites

Interfacial Enhancement by CNTs Grafting towards High-Performance Mechanical Properties of Carbon Fiber-Reinforced Epoxy Composites

Study on the Relationships between Microscopic Cross-Linked Network Structure and Properties of Cyanate Ester Self-Reinforced Composites

Improving the interfacial property of CF composites through constructing multiscale interfacial nanostructures

Hierarchical Curing Mechanism in Epoxy/bismaleimide Composites: Enhancing Mechanical Properties Without Compromising Thermal Stabilities

Mechanical and thermal properties of a novel bismaleimide matrix resin for high-performance composite materials

Through-thickness Thermal Conductivity Enhancement and Tensile Response of Carbon Fiber-Reinforced Polymer Composites

Unravelling the Influence of Surface Modification on the Ultimate Performance of Carbon Fiber/Epoxy Composites