Optical properties of blue‐light‐emitting Y2O3:Ce nanophosphor for solid‐state lighting application

M. Dutta,J.M. Kalita,G. Wary

DOI: https://doi.org/10.1002/bio.4718

IF: 2.613

2024-03-20

Luminescence

Abstract:The graphical abstract illustrates the XRD patterns of Y2O3:Ce (0%–5%) samples followed by steady‐state and time‐resolved photoluminescence emission spectra. It also includes colour coordinates associated with the dominant emission band of the samples recorded under 350 nm excitation. The structural, surface morphological, optical absorption and emission features of Y2O3:Ce (0%–5%) were studied. The samples had a body‐centred cubic crystal structure. The undoped sample had a crystallite size of 29.03 nm, and it varied after doping with Ce. The grain size of the samples varied from 23.00 to 50.78 nm. All the samples exhibited a strong absorption band at 206 nm due to F‐centre absorption and absorption involving the delocalised bands. In addition, the doped samples exhibited a secondary band at ~250 nm due to 4f → 5d transitions of Ce3+ ions. The optical bandgap of the undoped sample was found to be ~5.37 eV, and it decreased to 5.20 eV with an increase in Ce concentration to 5%. The undoped sample under 350‐nm excitation exhibited a broad photoluminescence (PL) emission band with the maxima at 406 nm and a secondary band at 463 nm. In contrast, multiple PL peaks were centred at ~397, 436, 466, 488 and 563 nm in all the doped samples. The average lifetime of the emission band at 406 nm was 1.05 ns and that of the emission band at ~466 nm was 1.63 ns. The material has potential for solid‐state lighting applications.

chemistry, analytical