Accelerating Li‐Ion Diffusion in LiFePO4 by Polyanion Lattice Engineering

Xinxin Wang,Anyang Yu,Tian Jiang,Shijun Yuan,Qi Fan,Qingyu Xu

DOI: https://doi.org/10.1002/adma.202410482

IF: 29.4

2024-10-12

Advanced Materials

Abstract:A polyanion lattice engineering strategy is applied on LiFePO4, with planar triangle BO33− substituting tetrahedron PO43− to induce more flexibility and provide additional paths between Li‐ion diffusion channels. These synergetically contribute to accelerate the Li‐ion diffusion, which have outstanding high‐rate and low‐temperature battery performances. This method may be extended to the other polyanionic materials. Despite the widespread commercialization of LiFePO4 as cathodes in lithium‐ion batteries, the rigid 1D Li‐ion diffusion channel along the [010] direction strongly limits its fast charge and discharge performance. Herein, lattice engineering is developed by the planar triangle BO33− substitution on tetrahedron PO43− to induce flexibility in the Li‐ion diffusion channels, which are broadened simultaneously. The planar structure of BO33− may further provide additional paths between the channels. With these synergetic contributions, LiFe(PO4)0.98(BO3)0.02 shows the best performance, which delivers the high‐rate capacity (66.8 mAh g−1 at 50 C) and long cycle stability (ultra‐low capacity loss of 0.003% every cycle at 10 C) at 25 °C. Furthermore, excellent rate performance (34.0 mAh g−1 at 40 C) and capacity retention (no capacity loss after 2500 cycles at 10 C) at −20 °C are realized.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology