Abstract:1.4418 hardened stainless steel (SS) is widely used in mechanical engineering because of its high functional properties. They can also be enhanced by procuring improvements in the state of the surface layer (SL) and, above all, in the factors of its strengthening, among others the average size of coherent scattering regions (ASCSR), dislocation density (DD), residual stresses (RS) of first and second orders, and relative micro-deformations of the crystal lattice (RMCL). This study investigates the effect of cutting speed ( v c ) ranging from 100 to 250 m/min and feed rate ( f ) ranging from 0.005 to 0.25 mm/rev on the indicators of SL condition after finish turning the steel tested. A reduction in ASCSR values below 8 nm was obtained for v c = 100–135 m/min, while an increase of ~ 20% was obtained for 180–250 m/min and with the f ranging from 0.2 to 0.25 mm/rev. An increase in RMCL of ~ 90% was registered for v c = 170–230 m/min and f = 0.2–0.25 mm/rev. A decrease in DD below 10 9 cm −2 was obtained for v c = 180–250 m/min and its ~ 25% increase for v c = 100–135 m/min. A high correlation between ASCSR and DD was shown. In the deformed material, the dislocation's resistance to motion increases in proportion to the increase in its density. A high linear correlation coefficient in the range of 0.8–0.9 is found between ASCSR, DD, and first-order RS on the one hand, and Sa and Sz surface texture parameters, which are used in the industry to assess product quality, on the other. Additionally, the effect of plastic side flow (PSF) was observed and described. When machining with v c = 119 m/min and f = 0.22 mm/rev, the intense plastic deformation of the material causes outflow and shearing of the surface micro-hills. Favorable compressive stresses (below − 100 MPa) were registered in the range of v c = 225–250 m/min at f = 0.005–0.05 m/rev and 0.2–0.25 mm/rev, as well as v c = 115–180 m/min and f = 0.05–0.17 mm/rev. The study proved the existence of a relationship between the cutting parameters and indicators of the thin crystalline structure of SL. This means that by proper controlling of these parameters, it is possible to obtain such a state of the SL workpiece, which will ensure its long-term use.

Effects of precipitation hardening on cutting force, surface roughness and tool wear in turning of 15‐5PH stainless steel

Effects of Cooling Rate on the Precipitation Behavior of Grain Boundary Carbide and Corrosion Resistance of 5cr15mov Stainless Steel

Effect of heat treatment parameters on microstructure and microhardness of 15-5PH stainless steel fabricated by selective laser melting

Influence of machining conditions on tool wear and surface characteristics in hot turning of AISI630 steel

Cutting Forces and Chip Shaping When Finish Turning of 17-4 PH Stainless Steel under Dry, Wet, and MQL Machining Conditions

Effects of Process Parameters on White Layer Formation and Morphology in Hard Turning of Aisi52100 Steel

Experimental Investigation of Surface Integrity in Finish Dry Hard Turning of Hardened Tool Steel at Different Hardness Levels

Effect of Heat Treatment on Microstructure and Performances of Additively Manufactured 15-5PH Stainless Steel

Effect of Solution Treatment on Microstructure and Properties of PH15-7Mo Semi-austenitic Precipitation Hardening Stainless Steel

Enhancement of machinability and surface tribological property of hardened bearing steel by electric pulse-assisted hard turning

Surface Integrity and Corrosion Resistance of 42CrMo4 High-Strength Steel Strengthened by Hard Turning

Processing of 17-4 PH steel in turning operation with hybrid textured tools

Fine evaluation of surface integrity of hardened 1.4418 stainless steel after finish dry turning

Experimental evaluation of different coated cutting tools effects on machinability in turning of 17-4 PH stainless steel and optimization of the cutting parameters

Experimental Analysis Of The Effect Of Mechanical Properties And Microstructure On Tool Vibration And Surface Quality In Dry Turning Of Hardened Aisi 4340 Steels

Machinability analysis of high strength materials with Cryo-Treated textured tungsten carbide inserts

Effects of shallow cryogenic treatment on surface characteristics and machinability factors in hard turning of AISI 4140 steel

Effect of Ranque-Hilsch Vortex Tube Cooling to Enhance the Surface-Topography and Tool-Wear in Sustainable Turning of Al-5.6Zn-2.5Mg-1.6Cu-0.23Cr-T6 Aerospace Alloy

Surface Integrity of Carbon Steel under Three Heat Treatment States Subjected to Orthogonal Turning Process

Sustainable Hard Machining of AISI 304 Stainless Steel Through TiAlN, AlTiN, and TiAlSiN Coating and Multi-Criteria Decision Making Using Grey Fuzzy Coupled Taguchi Method

Fracture Behavior of PH 15-5 Stainless Steel Manufactured via Directed Energy Deposition