Structure and mechanical properties anisotropy of a steel product manufactured by layer-by-layer electric arc wire 3D printing

I. V. Vlasov,A. I. Gordienko,A. E. Kuznetsova,V. M. Semenchuk

DOI: https://doi.org/10.17073/0368-0797-2023-6-709-717

2023-12-29

Abstract:The work presents the study of structure and mechanical properties anisotropy of a metal wall obtained using electric arc wire 3D printing (WAAM) with ER70S-6 wire. The layers were deposited in the protective gases of carbon dioxide and argon. As a result of structural studies, it was found that the internal structure of the model product in form of a wall can be divided into three zones. Repeated heating, cooling cycles and degree of accumulated heat influence the formation of different wall zones. As a result of rapid heat removal to the substrate during deposition of the first layers, the wall base (zone 1 ) contains large elongated grains with acicular ferrite structure. The wall middle part (zone 2 ) consists of ferrite-pearlite structure, which was formed as a result of recrystallization under conditions of repeated heating and cooling during 3D printing. The size of ferrite grains in zone 2 varies from 11 to 16.3 μm with increasing the number of layers. The gradual accumulation of heat during 3D printing led to the formation of structures in zone 3 under conditions of overheating and a reduced cooling rate. As a result, the wall upper part (zone 3 ) consists of large ferrite grains (up to 29.8 μm), sorbite, and a small proportion of Widemanstatten ferrite and acicular ferrite. It is shown that the most uniform level of mechanical characteristics (σ 0.2 = 340 MPa, σ u = 470 MPa, ε = 28 %) correspond to the samples cut from zone 2 in a direction parallel to 3D prin­ting direction. The samples cut in the vertical direction relative to 3D printing and from zone 3 show the lowest level of microhardness and mechanical characteristics (σ 0.2 = 260 MPa, σ u = 425 MPa, ε = 20 %).