Abstract:Here, a new Mg-1Bi-1Mn-0.3Zn (BMZ110, wt%) wrought alloy designed by the dilute addition of Zn subjected to an appropriate extrusion processing that showed an excellent strength-ductility synergy at room temperature. The main results included four aspects as follows: 1) With dilute Zn addition, the as-cast BMZ110 alloy was refined into an approximately equiaxed-grained structure, since the solid solution of Zn provided a relatively high growth restriction factor. 2) The as-extruded BMZ110 alloy exhibited the finer average grain size and weaker basal texture intensity than the as-extruded BM11 alloy without Zn. The co-segregation of Bi and Zn solutes into grain boundaries was observed to impede grain growth during extrusion and further weaken texture intensity. Moreover, Zn atoms incorporated into Mg3Bi2 phases by replacing Bi atoms increasing the nucleation rate of Mg3Bi2 phases and refining their sizes. 3) Compared with the as-extruded BM11 alloy, the as-extruded BMZ110 alloy demonstrated the higher yield strength (~ 283.4 MPa), ultimate strength (~ 366.2 MPa) and elongation-to-failure (~ 26%). The size refinement of grains and second phases contributed to an extra strength increments. Grain boundary segregation enhanced grain boundary cohesion not only reducing the number density of grain boundary cracks, but also activating more slip modes and grain rotation for increasing the ductility. 4) The as-extruded BMZ110 alloy had the higher grain growth resistance than the as-extruded BM11 alloy during annealing. Solute segregation offered an effective obstacle to restrict grain boundary migration enlarging the activation energy (~ 112.2 kJ/mol) and further delaying the grain growth. Therefore, this work will be helpful for the development of new high performance low-alloyed Mg-Bi based wrought alloys to achieve extensive applications in industries.

Strength–ductility synergy in Mg-Gd-Y-Zr alloys via texture engineering in bi-directional forging

Mechanism of Ductility Enhancement of the Mg-8Gd-4Y-1Nd-0.5Si Alloy by Multi-Directional Forging Process before Extrusion

Achieving High-Strength and Toughness in a Mg-Gd-Y Alloy Using Multidirectional Impact Forging

Enhancement of Ductility in High Strength Mg-Gd-Y-Zr Alloy

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Microstructure, texture and mechanical properties of coarse-grained Mg–Gd–Y–Nd–Zr alloy processed by multidirectional forging

Effect of Pack-Forging on Microstructure and Properties of Mg-Gd-Y-Zn-Zr Alloy

Achieving Ultra-High Strength in Mg–Gd–Ag–Zr Wrought Alloy Via Bimodal-Grained Structure and Enhanced Precipitation

Microstructure, Texture and Mechanical Properties of Extruded AZ31 Mg Alloy During Small Strain Multi-Directional Forging with Gradient Cooling

Improving Strength and Ductility of Mg–Gd–Y–Zn–Zr Alloy Simultaneously Via Extrusion, Hot Rolling and Ageing

Achieving Texture Randomization and Yield Anisotropy Reduction in Rolled Mg-Zn-Y-Zr Alloy by Multidirectional Impact Forging

Ductility enhancement in Mg–8.7Gd–4.18Y–0.42Zr magnesium alloy fabricated through extrusion and equal channel angular pressing (EX-ECAP)

Superior Strength-Ductility Synergy of Mg-Nd-Zn-Zr Alloy Rod Achieved by Drawing at Elevated Temperatures

Enhanced ductility and strength of Mg-1Zn-1Sn-0.3Y-0.2Ca alloy achieved by novel micro-texture design

High Strength and Ductility Mg-8Gd-3Y-0.5Zr Alloy with Bimodal Structure and Nano-Precipitates

Deformation Behavior of Ultra-Strong and Ductile Mg-Gd-Y-Zn-Zr Alloy with Bimodal Microstructure

Maximizing precipitation hardening effect enables ultrahigh strength in a coarse-grained Mg-13Gd forging alloy

Influence of Texture and Grain Size on the Room-Temperature Ductility and Tensile Behavior in a Mg–Gd–Zn Alloy Processed by Rolling and Forging

Exploiting an as-extruded fine-grained Mg-Bi-Mn alloy with strength-ductility synergy via dilute Zn addition

Evading Strength-Ductility Tradeoff in Mg Alloy via Uniform Microstructure and Unique Texture Modification Induced by Moderate Temperature ECAP

Towards strength-ductility synergy through a novel technique of multi-pass lowered-temperature drawing in AZ31 magnesium alloys