All-perovskite tandem solar cells with 3D/3D bilayer perovskite heterojunction

Renxing Lin,Yurui Wang,Qianwen Lu,Beibei Tang,Jiayi Li,Han Gao,Yuan Gao,Hongjiang Li,Changzeng Ding,Jin Wen,Pu Wu,Chenshuaiyu Liu,Siyang Zhao,Ke Xiao,Zhou Liu,Changqi Ma,Yu Deng,Ludong Li,Fengjia Fan,Hairen Tan
DOI: https://doi.org/10.1038/s41586-023-06278-z
IF: 64.8
2023-06-09
Nature
Abstract:All-perovskite tandem solar cells promise higher power-conversion efficiency (PCE) than single-junction perovskite solar cells while maintaining a low fabrication cost 1–3 . However, their performance is still largely constrained by the subpar performance of mixed Pb-Sn narrow-bandgap perovskite subcells, mainly due to a high trap density on the perovskite film surface 4–6 . Although heterojunctions with intermixed 2D/3D perovskites could reduce surface recombination, this common strategy induces transport losses and thereby limits device fill factors 7–9 . Here we develop an immiscible 3D/3D bilayer perovskite heterojunction with type-II band structure at the Pb-Sn perovskite/electron-transport layer interface to suppress the interfacial non-radiative recombination and facilitate charge extraction. The bilayer perovskite heterojunction is formed by depositing a layer of lead-halide wide-bandgap perovskite on top of the mixed Pb-Sn narrow-bandgap perovskite via a hybrid evaporation/solution processing method. This heterostructure allows us to increase the PCE of Pb-Sn perovskite solar cells having a 1.2-μm-thick absorber to 23.8%, together with a high open-circuit voltage ( V oc ) of 0.873 V and a high fill factor of 82.6%. We thereby demonstrate a record-high PCE of 28.5% (certified 28.0%) in all-perovskite tandem solar cell. The encapsulated tandem devices retain over 90% of their initial performance after 600 hours of continuous operation under simulated one-sun illumination.
multidisciplinary sciences
What problem does this paper attempt to address?
This paper mainly discusses the application of 3D/3D bilayer perovskite heterojunction in all-perovskite tandem solar cells to solve the problem of poor performance of mixed lead-tin narrow bandgap perovskite sub-cells. In the study, the authors developed a non-miscible 3D/3D bilayer structure by depositing a layer of lead halide wide bandgap perovskite on the mixed lead-tin narrow bandgap perovskite, forming a type-II energy band alignment interface, thereby suppressing non-radiative recombination and promoting charge extraction. This method improves the open-circuit voltage (Voc) and fill factor (FF) of the cells, achieving a high efficiency of 23.8% and a record-breaking efficiency of 28.5% (certified efficiency of 28.0%) in the tandem solar cells. The paper points out that the performance of mixed lead-tin perovskite bottom cells is limited by high surface trap density, while the 2D/3D heterojunction can reduce surface recombination, but may lead to transmission loss and higher series resistance. Therefore, they designed a novel 3D/3D heterojunction, which avoids damage to the bottom perovskite through a non-destructive two-step deposition method, successfully reducing non-radiative recombination and improving the efficiency and stability of the devices. The encapsulated tandem devices can maintain over 90% of their initial performance after 600 hours of continuous illumination.