All-perovskite tandem solar cells with 24.2% certified efficiency and area over 1 cm2 using surface-anchoring zwitterionic antioxidant

Ke Xiao,Renxing Lin,Qiaolei Han,Yi Hou,Zhenyuan Qin,Hieu T. Nguyen,Jin Wen,Mingyang Wei,Vishal Yeddu,Makhsud I. Saidaminov,Yuan Gao,Xin Luo,Yurui Wang,Han Gao,Chunfeng Zhang,Jun Xu,Jia Zhu,Edward H. Sargent,Hairen Tan

DOI: https://doi.org/10.1038/s41560-020-00705-5

IF: 56.7

2020-10-05

Nature Energy

Abstract:Monolithic all-perovskite tandem solar cells offer an avenue to increase power conversion efficiency beyond the limits of single-junction cells. It is an important priority to unite efficiency, uniformity and stability, yet this has proven challenging because of high trap density and ready oxidation in narrow-bandgap mixed lead–tin perovskite subcells. Here we report simultaneous enhancements in the efficiency, uniformity and stability of narrow-bandgap subcells using strongly reductive surface-anchoring zwitterionic molecules. The zwitterionic antioxidant inhibits Sn²⁺ oxidation and passivates defects at the grain surfaces in mixed lead–tin perovskite films, enabling an efficiency of 21.7% (certified 20.7%) for single-junction solar cells. We further obtain a certified efficiency of 24.2% in 1-cm²-area all-perovskite tandem cells and in-lab power conversion efficiencies of 25.6% and 21.4% for 0.049 cm² and 12 cm² devices, respectively. The encapsulated tandem devices retain 88% of their initial performance following 500 hours of operation at a device temperature of 54–60 °C under one-sun illumination in ambient conditions.

materials science, multidisciplinary,energy & fuels

What problem does this paper attempt to address?

The paper aims to address several key issues in mixed Pb–Sn perovskite solar cells, including efficiency, uniformity, and stability. Specifically:

1. **Efficiency Improvement**: By adding a surface-anchored zwitterionic antioxidant (formamidine sulfinic acid, FSA) to the precursor solution, researchers significantly enhanced the power conversion efficiency (PCE) of narrow-bandgap perovskite solar cells. Experimental results showed that the highest efficiency of single-junction cells reached 21.7%, with a certified efficiency of 20.7%.

2. **Uniformity Improvement**: The addition of FSA not only inhibited the oxidation of Sn²⁺ but also passivated defects on the grain surfaces, thereby improving the quality uniformity of the perovskite films. This resulted in more consistent performance for large-area devices (e.g., 1 square centimeter).

3. **Stability Enhancement**: The study found that under encapsulated conditions, after 500 hours of continuous operation at temperatures between 54–60°C, the tandem solar cells were able to maintain 88% of their initial performance.

In summary, the paper primarily addresses several core challenges in mixed Pb–Sn perovskite solar cells, including high defect density, susceptibility to oxidation, and film non-uniformity, and successfully achieves highly efficient and stable all-perovskite tandem solar cells.