Effects of post‐curing light intensity on the trueness, compressive strength, and resin polymerization characteristics of 3D‐printed 3‐unit fixed dental prostheses
Citra Dewi Sahrir,Wei‐Shao Lin,Chin‐Wei Wang,Wei‐Chun Lin
DOI: https://doi.org/10.1111/jopr.13951
2024-09-13
Journal of Prosthodontics
Abstract:Purpose To investigate the effect of different post‐curing light intensities on the trueness, compressive strength, and resin polymerization of 3D‐printed 3‐unit fixed dental prostheses (FPD). Materials and Methods A total of 60 specimens were prepared to support a 3‐unit FDP with a deep chamfer marginal design, utilizing computer‐aided design and computer‐aided manufacturing (CAD‐CAM) technology. Light‐polymerizing FDP resin with varying light intensities (105, 210, 420, and 840 mW/cm2) was employed for 10 min. Subsequently, trueness assessment, fracture load testing, scanning electron microscopy (SEM) surface examination, and Fourier‐Transform Infrared (FTIR) analysis were conducted. A one‐way analysis of variance (ANOVA) was performed to ascertain the differences between the experimental groups (p < 0.05). Results The group exposed to 210 mW/cm2 showed the highest trueness (57.6 ± 2.1 μm), while the 840 mW/cm2 group had the highest deviation (79.3 ± 2.7 μm) (p < 0.001). Significant differences in fracture resistance were found between groups (p < 0.001), with mean fracture strengths of 1149.77 ± 67.81 N, 1264.92 ± 39.06 N, 1331.34 ± 53.62 N, and 1439.93 ± 34.58 N for light intensities of 105, 210, 420, and 840 mW/cm2, respectively (p < 0.001). The resin polymerization analysis shows a peak intensity surge at 3579 cm−1 for O‐H and C‐H stretching vibrations, except in samples exposed to 105 mw/cm2 light, with the lowest peak at 2890 cm−1. The performance of resin polymerization is most significant under the condition of 840 mW/cm2. Conclusion The light intensity of 210 mW/cm2 exhibited the highest trueness, while the 840 mW/cm2 group showed the highest deviation. However, the light intensity of 840 mW/cm2 demonstrated the highest compressive strength. Furthermore, polymerization occurred at all post‐treatment light intensities except 105 mW/cm2. These findings indicate that while low‐intensity usage offers greater trueness, high‐intensity usage provides better compressive strength and polymerization. Therefore, 210 mW/cm2 could be the recommended solution for post‐curing.
dentistry, oral surgery & medicine