Abstract:In this article we report magnetite (Fe 3 O 4 ) nanoparticles prepared via hydrothermal technique at different reaction time and precursor's concentration. X-ray diffraction (XRD) result shows the formation of single phase iron oxide that matches well with standard JCPDS card #: 01-079-0418. Excellent crystallinity was achieved for octahedral shape particles (∼150 nm) as compared to porous spherical shape Fe 3 O 4 particles (∼250 nm) which is supported by field emission scanning electron microscope images (FESEM). Fourier transform infrared spectroscopy (FTIR) results show strong peak at 540 cm −1 for both samples indicating Fe–O–Fe bending vibration and formation of chemical bonding characteristic of Fe 3 O 4 lattice structure. The electrical transport properties show that correlated barrier hopping (CBH) between Fe 3+ and Fe 2+ ions, is the possible operating conduction mechanism in both samples and octahedral shape Fe 3 O 4 nanoparticles are more conductive than porous spherical shape particles. The corresponding activation energies of grain and grain boundary for octahedral and porous spherical shape Fe 3 O 4 nanoparticles are ∼0.197 & ∼0.292eV and ∼0.226 & ∼0.30eV, respectively. Furthermore, dielectric constant of the octahedral shape Fe 3 O 4 nanoparticles is high due to its low energy losses and high value of crystallinity as compared to spherical shape particles. Magnetic properties show ferrimagnetic nature of both Fe 3 O 4 samples. Corresponding high values of magnetic saturation, coercivity , and remanent magnetization of octahedral shape Fe 3 O 4 particles are 71emu/g, 123 Oe, and 10.6 emu/g, respectively, which indicates the influence of magnetic properties on the grain size, crystallinity and morphology of the constituent particles.

Solvothermal synthesis and characterization of Iron oxide nanoparticles

Synthesis and Characterisation of Transition Metal Iron Oxide Nanocomposite Crystals and Particles Using Wet Chemical Coprecipitation Method

Solvothermal Synthesis and Properties of Monodisperse Magnetite Nanoparticles

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Study of the Solvothermal Method Time Variation Effects on Magnetic Iron Oxide Nanoparticles (fe3o4) Features

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Synthesis, characterization, and dielectric studies of magnetic iron oxide nanoparticles

Synthesis and Characterization of Fe3O4 Nanoparticles by a Solvothermal Method

Solvothermal Synthesis of Monodisperse Iron Oxides with Various Morphologies and Their Applications in Removal of Cr(vi)

Solvothermal synthesis and characterization of size-controlled monodisperse Fe 3 O 4</s

Solvothermal Synthesis of Size-Controlled Monodispersed Superparamagnetic Iron Oxide Nanoparticles

Solvothermal synthesis and characterization of size-controlled monodisperse Fe 3 O 4 nanoparticles

A Facile Solvothermal Synthesis of Octahedral Fe3 O4 Nanoparticles.

Controllable synthesis of monodispersed iron oxide nanoparticles by an oxidation-precipitation combined with solvothermal process

Solvothermal synthesis and characterization of size-controlled monodisperse Fe<sub>3</sub>O<sub>4</sub> nanoparticles

Solvothermal reduction synthesis and characterization of superparamagnetic magnetite nanoparticles

Synthesis, Characterizations, and Applications of Fe3O4 and Co-Doped Fe3O4 Nanomaterials

Advance in preparation of Fe3O4 nanoparticles by solvothermal method

Temperature Effects on the Structural, Morphological, and Magnetic Properties of Iron Oxide Nanoclusters Using Solvothermal Method

Solvothermal synthesis of Sm3+-doped Fe3O4 nanoparticles

Investigation of size-dependent electrical, dielectric, and magnetic properties of iron oxide nanostructures