Abstract:Synthesis methods of composites. Copper‐based metal–organic frameworks is anticipated to find applications in the field of friction materials owing to its plentiful surface‐active groups and distinctive framework structure. In this study, copper‐based metal–organic frameworks was synthesized through ultrasound‐assisted method and incorporated alone into carbon fiber reinforced epoxy composites or together with SiO2 nanoparticles towards the goal of improving the composites' friction and wear properties. It is revealed that copper‐based metal–organic frameworks alone cannot improve the friction and wear of carbon fiber reinforced epoxy composites simultaneously. The combination of copper‐based metal–organic frameworks and SiO2 nanoparticles was more effective in enhancing both the mechanical and tribological properties of studied composites. The composite material exhibits a friction coefficient of 0.104 under the specified test conditions of 10 MPa and 3.75 m/s. Additionally, the specific wear rate is impressively low, measuring only 5.64 × 10−7 mm3 N/m. Through morphological and chemical analysis on the worn surfaces and transfer films, the functioning mechanism of copper‐based metal–organic frameworks in modifying the mechanical and tribological properties was discussed. It was discovered that a tribological synergy exists between short carbon fibers, copper‐based metal–organic frameworks, and SiO2 fillers, leading to a shift in the wear mechanism of the composite materials from abrasive wear to adhesive wear. Concurrently, a shear‐prone transfer film forms on the surface of the counter steel surfaces. Findings of the present study pave a new route of designing high performance epoxy based tribo‐composites by using metal–organic frameworks. Highlights Cu‐BDC nanosheets were synthesized using ultrasound‐assisted techniques and incorporated as tribological fillers in EP composites. The combined use of Cu‐BDC, SiO2, and SCF fillers synergistically enhances the mechanical and tribological properties of EP composites. The composite material exhibits a friction coefficient of 0.104 under the specified test conditions of 10 MPa and 3.75 m/s, the specific wear rate is impressively low, measuring only 5.64 × 10−7 mm3N/m. During the sliding friction process of the composite materials, Cu‐BDC and SiO2 play a crucial role in reducing SCF pull‐out wear through their anchoring effect. The dynamic coordination bond structure of Cu‐BDC contributes to the formation of uniform and continuous transfer films on counter metal surfaces.

Effect of Bimodal Structure on the Frictional Properties of Copper–Graphite Composites

Wear resistance mechanism of graphene/copper composite foils with bimodal structure

Effect of Copper-Plated Graphite Content on the Microstructure and Properties of Copper-Graphite Composites Prepared by Spark Plasma Sintering

Study on the Tribological Performance of Copper-Based Powder Metallurgical Friction Materials with Cu-Coated or Uncoated Graphite Particles as Lubricants

On the tribological behaviors of Cu matrix composites with different Cu-coated graphite content

Tribological synergy of copper‐based metal–organic frameworks, carbon fibers and SiO2 in modifying the friction and wear properties of epoxy composites

Characterization and Tribological Properties of Graphene/Copper Composites Fabricated by Electroless Plating and Powder Metallurgy

Wear Mechanism of Copper-based Powder Metallurgical Friction Materials with Different Graphite Content

Effect of sintering temperature on microstructure and tribological properties of copper/graphite composites doped with Ti3AlC2 particles

Superior mechanical properties and wear resistance of copper/graphite metallic composites fabricated with fibrous copper powder

Wear and friction behaviour of Cu-Gr-B4C composites and correlating to the topographical characteristics

Remarkable anisotropic wear resistance with 100-fold discrepancy in a copper matrix laminated composite with only 0.2 vol% graphene

Tribological and Wear Properties of Cu-Based Composite Reinforced by Core–Shell Structure in Multi-disk Clutch

Synergetic influence of TiCnp and graphite particles on tribological performance of Cu based composites prepared by flake powder metallurgy

Study on the tribological properties of MoB/Cu laminated composite materials fabricated by hot-pressing process

Synergistic Effects of Different Graphite on the Braking Performance of Cu-Matrix Friction Materials for High-Speed Trains Based on Pin–Disc Tests

Study of Friction and Wear Properties of Cu/Short Carbon Fibers Composites

Microstructure, mechanical and tribological properties of Cu-Sn/Cr3C2/Gr composites

Low Friction Coefficient Bioinspired Copper/graphene Nanolaminates with High Content Graphene

Effect of ball-milling and graphene contents on the mechanical properties and fracture mechanisms of graphene nanosheets reinforced copper matrix composites

Tribological behavior and mechanism of h-BN modified copper metal matrix composites paired with C/C–SiC