To enhance the molecular aggregation and decrease the optical gap by the dual-additive to reduce the energy loss of all-polymer organic solar cells

Jiaqi Pan,Qiang Zhang,Jian Guan,Hanyue Gao,Luzhuo Li,Rui Zhang,Hongxiang Li,Xinhong Yu,Yanchun Han

DOI: https://doi.org/10.1039/d4tc03309d/v2/review1

IF: 6.4

2024-11-26

Journal of Materials Chemistry C

Abstract:All-polymer solar cells (all-PSCs) have attracted significant attention due to their unique advantages, such as intrinsic stretchability and high thermal stability. However, in the PM6:PYIT system, the control of phase-separated aggregation size of the acceptor PYIT is particularly crucial because of the difficulties in choosing the suitable solvents. High-boiling-point solvents such as chlorobenzene may lead to excessive aggregation of the acceptor due to the slow solvent evaporation and, the low-boiling-point solvents like chloroform (CF) may result in small aggregation sizes of the acceptor due to its fast evaporation. To optimize the aggregation size of the acceptor PYIT, we employ a strategy of using two high-boiling-point solvent additives (diphenyl ether: DPE and chloronaphthalene: CN) to prolong the aggregation and film formation time of the acceptor PYIT. The result shows that the aggregation state of PYIT was optimized effectively after the evaporation of CF, by the slow evaporation process of DPE and CN acts synergistically. Moreover, DPE with lower surface energy tends to make PM6 aggregate more in the bottom anode region, while CN with higher surface energy drives PYIT to aggregate upwards, forming a vertical phase separation distribution structure, which is conducive to efficient exciton dissociation and charge transport. Further analysis indicates that the introduction of the dual-additive leads to a corresponding increase in the external quantum efficiency (EQE) spectrum and an effective reduction in the absorption bandgap (Eg) of the solar cells. Consequently, the PCE of the optimized device increases notably, from 14.58% to 16.67% and a reduction in Eloss from 0.500 eV to 0.476 eV by adding 0.6 vol% of 1-CN and 0.4 vol% of DPE simultaneously.

materials science, multidisciplinary,physics, applied