The Formation of Sp 3 Bonding in Compressed BN
Yue Meng,Ho-kwang Mao,Peter J. Eng,Thomas P. Trainor,Matthew Newville,Michael Y. Hu,Chichang Kao,Jinfu Shu,Daniel Hausermann,Russell J. Hemley
DOI: https://doi.org/10.1038/nmat1060
IF: 41.2
2004-01-01
Nature Materials
Abstract:Attributed to their specific atomic bonding, the soft, graphite-like, hexagonal boron nitride (h-BN) and its superhard, diamond-like, cubic polymorph (c-BN) are important technological materials with a wide range of applications 1 . At high pressure and temperature, h-BN can directly transform to a hexagonal close-packed polymorph (w-BN) 2 that can be partially quenched after releasing pressure. Previous theoretical calculations 3 , 4 , 5 and experimental measurements (primarily on quenched samples) 6 , 7 , 8 , 9 provided substantial information on the transition, but left unsettled questions due to the lack of in situ characterization at high pressures. Using inelastic X-ray scattering to probe the boron and nitrogen near K-edge spectroscopy, here we report the first observation of the conversion process of boron and nitrogen sp 2 - and p -bonding to sp 3 and the directional nature of the sp 3 bonding. In combination with in situ X-ray diffraction probe, we have further clarified the structure transformation mechanism. The present archetypal example opens two enormous, element-specific, research areas on high-pressure bonding evolutions of boron and nitrogen; each of the two elements and their respective compounds have displayed a wealth of intriguing pressure-induced phenomena 10 that result from bonding changes, including metallization 11 , 12 , superconductivity 13 , 14 , semiconductivity 15 , polymerization 16 and superhardness 2 , 17 , 18 .