Abstract:Hydrogen is considered one of the most likely alternative clean energy fuel to traditional fossil fuels. One of the most attractive hydrogen production strategies is water splitting, but the need for expensive Pt precious metal catalysts to catalyze the hydrogen evolution reaction (HER) is a problem. Recently, two-dimensional transition metal dichalcogenides (TMDs), especially MoS2, have attracted intense interest as a non-precious metal HER catalyst due to their low cost and relatively high catalytic activity. However, their poor electron conductivity and the limited number of active sites at their edges have greatly limited their overall catalytic performance. We report the direct growth of three representative TMDs (MoS2, NbS2 and WS2) on a conductive carbon paper substrate using chemical vapor deposition and have studied the effects of temperature and gas flow rate on their morphology and structure. All the as-grown TMDs have a 2D nanosheet morphology and were aligned perpendicular to the carbon paper. The WS2 nanosheets had the smallest sheet size with a diameter of ca. 100-200 nm and, more interestingly, were assembled into a one-dimensional nanofiber, leading to the highest HER activity. Additional electrochemical cathodic activation further improved the HER activity of the TMDs, and the structural changes after the activation were investigated by TEM combined with in-situ electrochemical Raman spectroscopy. The activated NbS2 contained large triangular or truncated triangular S vacancy areas, which is distinctly different from the individual S vacancies in MoS2.

Chemical vapor deposition of uniform bilayer PtS2 flakes for electrocatalytic hydrogen evolution

Unveiling the Layer‐Dependent Catalytic Activity of PtSe2 Atomic Crystals for the Hydrogen Evolution Reaction

Synthesis of ultrathin PdSe2 flakes for hydrogen evolution reaction

Sulfur Vacancy Riched Pure 2H Phase VS2 for Efficient Electrocatalytic Hydrogen Evolution

Activating a Two-Dimensional PtSe2 Basal Plane for the Hydrogen Evolution Reaction Through the Simultaneous Generation of Atomic Vacancies and Pt Clusters.

Chemical Vapor Deposition of Monolayer WS2 Nanosheets on Au Foils Toward Direct Application in Hydrogen Evolution

Chemical Vapor Deposition Grown Large-Scale Atomically Thin Platinum Diselenide with Semimetal-Semiconductor Transition

Morphology-controlled growth of large-area PtSe2 films for enhanced hydrogen evolution reaction

Controllable Growth and Defect Engineering of Vertical PtSe2 Nanosheets for Electrocatalytic Hydrogen Evolution

Large-Substrate-Terrace Confined Growth of Arrayed Ultrathin PtSe2 Ribbons on Step-Bunched Vicinal Au(001) Facets Toward Electrocatalytic Applications

Controllable Growth and Defect Engineering of Vertical PtSe 2 Nanosheets for Electrocatalytic Hydrogen Evolution

Directly grown monolayer MoS2 on Au foils as efficient hydrogen evolution catalysts

Dendritic, Transferable, Strictly Monolayer MoS2 Flakes Synthesized on SrTiO3 Single Crystals for Efficient Electrocatalytic Applications

Layer-dependent Electrocatalysis of MoS2 for Hydrogen Evolution

Application of Chemical Vapor–deposited Monolayer ReSe2 in the Electrocatalytic Hydrogen Evolution Reaction

Interfacial electronic structure modulation of Pt-MoS2 heterostructure for enhancing electrocatalytic hydrogen evolution reaction

Efficiently Synergistic Hydrogen Evolution Realized by Trace Amount of Pt-Decorated Defect-Rich SnS2 Nanosheets.

CHEMICAL VAPOR DEPOSITION OF TWO-DIMENSIONAL TRANSITION METAL SULFIDES ON CARBON PAPER FOR ELECTROCATALYTIC HYDROGEN EVOLUTION CATALYTIC ACTIVITY

Two-dimensional Pt2P3 monolayer: A promising bifunctional electrocatalyst with different active sites for hydrogen evolution and CO2 reduction

Large-Scale, Controllable Synthesis of Ultrathin Platinum Diselenide Ribbons for Efficient Electrocatalytic Hydrogen Evolution

Realizing the Excellent HER Performance of Pt 3 Pb 2 S 2 by d-Orbital Electronic Modulation