Abstract:A range of Fe-Cr-Ni alloys are used in nuclear power plants due to their high mechanical strength and corrosion resistance. As a major component of these alloys, Ni contributes to the formation of austenite microstructures. In many nuclear reactor applications the alloys are exposed to ionizing radiation (g-rays) that can continuously decompose water to a range of highly redox active species (such as •OH, H2O2, O2). The change in water chemistry induced by radiation can affect both the general and localized corrosion behaviour of these alloys. In particular, its influence on the susceptibility of an alloy to localized corrosion such as crevice and stress corrosion cracking (SCC) are important for assessment of reactor component aging. As well, corrosion products that dissolve into the reactor coolant can be transported to the reactor core where they can be neutron activated. This can create a radiological hazard for reactor maintenance personnel. Thus, quantifying the rate of general corrosion and the corrosion product transport in a reactor are important safety, operation and maintenance issues. It has been well established that the type of oxide that forms on a surface is a critical factor in determining both general and localized corrosion behaviour. Both alloy composition and water chemistry affect the type of oxide that forms. Systematic studies that examine the effect of alloy composition on corrosion are rare and those available have been conducted mostly from a metallurgical perspective. There are even fewer studies that examine the combined effects of alloy composition and corrosion environment. A fundamental understanding of the mechanism by which the Fe to Ni ratio in a steel alloy influences the corrosion rate in different environments will provide valuable information that can be used for alloy selection and usage. We have investigated the effect of the Fe to Ni ratio of alloy on oxide formation and growth kinetics. For this study, customized steel alloys with different Ni contents and constant Cr content (18 ± 1 %) were prepared. The Ni content ranged from 15 to 25 wt.%, within the range between AISI 316L and Alloy 800 (Fig. 1). The corrosion kinetics was investigated using a combination of coupon corrosion tests and electrochemical measurements. These measurements were augmented by oxide surface and depth analyses using several spectroscopic and imaging techniques, and by post-test solution analyses for dissolved metal loss. We found that the oxide formed at pH 10.6 and 80 °C has a graded layer structure, consisting of a mixed spinel oxide (FeCr2O4/Fe3O4/NiFe2O4) as an inner layer and Ni(OH)2 as an outer layer. The increase in Ni content from 15 to 25 wt.% does not affect the inner layer but increases the thickness of the Ni(OH)2 layer. The increase in Ni content also decreases the total amount of dissolved metal loss. Gamma-irradiation of the corroding system increases the corrosion potential on these alloys. Correspondingly, gamma-radiation accelerates the formation of passive oxide layers and decreases the overall rate of metal dissolution. The observed kinetics of oxide growth and metal dissolution can be explained by the competition kinetics of oxide growth and dissolution for oxidized metals. Figure 1

High temperature electrochemical reaction parameters affecting electrochemical corrosion potential of nickel-base Alloy 82 weld metal

Corrosion behavior for Alloy 690 and Alloy 800 tubes in simulated primary water

CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR

Study on High-Temperature Naphthenic Acid Corrosion of Type 304 and Type 316L Stainless Steel and Their Welded Joints

Corrosion Behavior of Alloy 800 in Naoh and Eta Solutions at 300 Degrees C

Effect of Nickel Content on the Corrosion Behaviour of Stainless Steel at 80 °C

Influence of Alloying Element on Corrosion Behavior of Hastelloy C-276 in Supercritical Water

Selected corrosion behaviors of a Cu0.5NiAlCoCrFeSi bulk glassy alloy in 288°C high-purity water

Corrosion characteristics of a nickel-base alloy C-276 in harsh environments

Corrosion Properties of a Novel Bulk Cu0.5NiAlCoCrFeSi Glassy Alloy in 288 °C High-Purity Water

Localized Corrosion Resistance of Nickel Alloy 718 In Chloride-Containing Environments

Effects of alternating dissolved oxygen and dissolved hydrogen on the corrosion behavior of alloy 52 in high temperature high pressure water

Corrosion Behavior of FeCoNiCrAl High-Entropy Alloy in Molten NaNO3-KNO3

Electrochemical corrosion behaviour of Alloy 690 in simulated PWR high temperature aqueous environments

Influence of Temperature on Electrochemical Behavior and Oxide Film Property of Alloy 800 in Hydrogenated High Temperature Water

Effect of Low Oxygen Concentration on the Oxidation Behavior of Ni-based Alloys 625 and 825 in Supercritical Water

Effect of Salt Deposits on Corrosion Behavior of Ni-Based Alloys in Supercritical Water Oxidation of High-Salinity Organic Wastewater

In-Situ Electrochemical Corrosion Behavior of Nickel-Base 718 Alloy under Various CO2 Partial Pressures at 150 and 205 °C in NaCl Solution

Corrosion Behavior of Different Parts of the Weld of 316l/52m/a508 Dissimilar Metal Welded Joint in Simulated Pressurized Water Reactor Primary Water

Corrosion Behavior of Ni-Based Alloys in Supercritical Water Containing High Concentrations of Salt and Oxygen

EIS study of oxidation heat‐treatment effects on corrosion behavior of Ni10Cu11Fe6Al metallic inert anode inside molten calcium chloride salt