Abstract:Highlights • A metal–organic framework, Mn-MOF ([Mn(DMF) 2 (H 2 DHTPA)] n ) was synthesized. • Mn-MOF-500 was prepared using Mn-MOF through 500°C carbonization. • The BET surface area of Mn-MOF-500 is 11.83 m 2 /g. • The q max of Mn-MOF-500 on Pb II , As V , As III are 356.2, 166.1, 51.3 mg/g, respectively. • The q max of Mn-MOF-500 on PO 4 3- , Cd II , Cu II are 126.9, 88.5, 146.9 mg/g, respectively. Metal–organic frameworks (MOFs) are adsorbents suitable for water treatment. However, they are often water soluble and poorly processible, limiting their industrial applications. This study aims to develop a carbonized MOFs with high adsorption performance based on MOFs. Here, we report the production of Mn-MOF [Mn(DMF) 2 (H 2 DHTPA)] n (where DMF is N , N -dimethylformamide and H 4 DHTPA is 2,5-dihydroxyterephthalic acid) via a solvothermal method. This MOF shows good adsorption performance for various ions but dissolves easily in water. However, Mn-MOF-500 which was obtained by carbonising Mn-MOF at 500 °C shows high water stability. Thus, the adsorption properties of Mn-MOF-500 were investigated, revealing adsorption capacities for PO 4 3- , Cd(II), Pb(II), Cu(II), As(III), and As(V) of 126.66, 88.46, 356.21, 146.92, 51.28, and 166.10 mg/g, respectively. Based on the adsorption isotherms and the adsorption kinetics, the adsorption of PO 4 3- , Cd(II), and As(III) occurs via monolayer chemisorption, whereas that of Pb(II), Cu(II), and As(V) occurs via monolayer chemisorption and physisorption in pores. X-ray diffractometry and X-ray photoelectron spectroscopy analysis showed that P, Cd(II), Pb(II), Cu(II), As(III), and As(V) were adsorbed on Mn-MOF-500 as PO 4 3- , Cd(OH) 2 , PbO and Pb(OH) 2 , Cu(OH) 2 , Mn 3 (AsO 3 ) 2 , and MnHAsO 4 , respectively. Graphical abstract Download : Download high-res image (45KB) Download : Download full-size image

Enhanced Mechanical Stability and Proton Conductivity Performance from the Dense Mn(II)-Metal-Organic Framework to Porous Mn(II)-Fe(III)-Metal-Organic Framework

Crystal Structures and Proton Conductivities of A Mof and Two Pom-Mof Composites Based on Cu-Ii Ions and 2,2 '-Bipyridyl-3,3 '-Dicarboxylic Acid

A 3D POM-MOF composite based on Ni(II) ion and 2,2′-bipyridyl-3, 3′-dicarboxylic acid: Crystal structure and proton conductivity

Fabrication and Electrochemical Performance of Nanofibrous Micro-Frameworks of Α-Mno2

A Three-Dimensional Porous Mn(II)-Metal–Organic Framework Based on a Caged Structure Showing High Room-Temperature Proton Conductivity

Enhanced proton conductivity by guest molecules exchange in an acylamide-functionalized metal-organic framework

Enhancement of Proton Conductivity in Nonporous Metal–Organic Frameworks: the Role of Framework Proton Density and Humidity

Tuning the Ionicity of Stable Metal–Organic Frameworks Through Ionic Linker Installation

Water-Mediated Proton Conduction in Metal–Organic Frameworks with High Water Stability Constructed by a Terpyridine Tricarboxylate Ligand

Acidic Groups Functionalized Carbon Dots Capping Channels of a Proton Conductive Metal–Organic Framework by Coordination Bonds to Improve the Water-Retention Capacity and Boost Proton Conduction

Metal Effect on the Proton Conduction of Three Isostructural Metal-Organic Frameworks and Pseudo-Capacitance Behavior of the Cobalt Analogue

Proton Conducting Metal‐Organic Frameworks (MOFs) via Post Synthetic Transmetallation and Water Induced Structural Transformations

High H2O-Assisted Proton Conduction in One Highly Stable Sr(II)-Organic Framework Constructed by Tetrazole-Based Imidazole Dicarboxylic Acid

Multiple Strategies to Fabricate a Highly Stable 2D Cu II Cu I –Organic Framework with High Proton Conductivity

Metalo Hydrogen-Bonded Organic Frameworks Constructed by Coordinated Chains for Magnetic and Proton-Conductive Bifunctionality

Structural Elucidation and Supercapacitive Performance on a Mn(II)-Based MOF

Adsorption of PO 4 3- , Cd(II), Pb(II), Cu(II), As(III), and As(V) using a carbonised Mn-based metal–organic framework

Enhancing Hydrogen Adsorption Capacity of Metal Organic Frameworks M()TED through Constructing a Bimetallic Structure.

Boosting the Proton Conduction in a Magnetic Dysprosium-Organic Framework by Introducing Conjugate NH4+-NH3 Pairs

Improving Proton-Conducting Stability by Regulating Pore Size of MOF Materials through Mixed Grinding

A Comparison of Two Isoreticular Metal–Organic Frameworks with Cationic and Neutral Skeletons: Stability, Mechanism, and Catalytic Activity