Abstract:Compared with the crystalline transition metal oxyhydroxide, low-crystalline structure is conducive to high electrochemical performance due to its more grain boundaries and ion diffusion channels. However, the manufacture of low-crystalline oxyhydroxides remains challenging, especially those with multiple transition metals. Herein, high mass loading (∼9 mg cm−2) and low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth (CC) were prepared by electrochemical reconstruction. The low-crystalline Ni/Co-oxyhydroxides nanoarrays possessed a hierarchical structure, which were consist of flake-like (Co0.25, Ni0.75)O(OH) single-crystals and needle-like Ni-doped CoO(OH) polycrystalline. Both single crystal nanoflakes and polycrystalline nanoneedles contained a lot of defects. Owing to the unique structure, the mutual doping of Ni and Co atoms, and the abundant defects, the nanoarrays of Ni/Co-3500 showed excellent electrochemical performance with a high specific capacitance of 8.87 F cm−2 at 5 mA cm−2 and a high rate retention of 69.33% at 50 mA cm−2, as well as a high cycle stability remaining 91.6% of initial capacitance after 2000 galvanostatic charge-discharge cycles at a current density of 20 mA cm−2. Furthermore, the assembled asymmetric supercapacitor of Ni/Co-3500//oxidized CC delivered a high areal capacitance of 1.48 F cm−2 and a volumetric capacitance of 14.8 F cm−3 at 8 mA cm−2, as well as 1.11 F cm−2 (11.1 F cm−3) even at 50 mA cm−2. The energy density of Ni/Co-3500//oxidized CC device was up to 4.35 mWh cm−3 at the powder density of 60.1 mW cm−3. It indicates that the as-prepared low-crystalline Ni/Co-oxyhydroxides arrays on CC is a promising electrode for high energy density supercapacitors.

Effects of ammonium chloride on structural stability of cobalt carbonate hydroxide and their improved electrochemical performance for supercapacitor

Formation of Bimetallic Metal-Organic Framework Nanosheets and Their Derived Porous Nickel-Cobalt Sulfides for Supercapacitors.

Co3O4@CoNi-LDH Core/shell Nanosheet Arrays for High-Performance Battery-Type Supercapacitors

The synergistic effect of NiCo2S4 and carbon nanosheets for supercapacitor: Enhanced adsorption/desorption of OH- on Ni and Co active sites

Morphology modulation of cobalt-based nano-oxides and their use as high-performance supercapacitor electrode materials

Core-shell structured MgCo2O4@Ni(OH)2 nanorods as electrode materials for high-performance asymmetric supercapacitors

Construction of Core-Shell Cobalt Sulfide/manganese Molybdate Nanostructure on Reduced Graphene Oxide/ni Foam As an Advanced Electrode for High-Performance Asymmetric Supercapacitor

Growth of uniform CuCo2O4 porous nanosheets and nanowires for high-performance hybrid supercapacitors

Low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth with high mass loading and hierarchical structure as cathode for supercapacitors

Construction of Double-Shell Basic Cobalt/Nickel Carbonate Microspheres via MOFs Etching Strategy for Boosting Aqueous Supercapacitor Performances

Facile fabrication 1D/2D/3D Co3O4 nanostructure in hydrothermal synthesis for enhanced supercapacitor performance

Electroconversion synthesis of Ni/Co layered nanomaterials for high-performance supercapacitors

Growth of CoMn-LDH/Co-Ni Bimetallic Sulfides on Nickel Foam with Enhanced Electrochemical Properties for Asymmetric Supercapacitors

Nickel/cobalt bimetallic metal-organic frameworks ultrathin nanosheets with enhanced performance for supercapacitors

NiCoMn-LDH with core-shell heterostructures based on CoS nanotube arrays containing multiple ion diffusion channels for boosted supercapacitor applications

A crystalline nickel vanadium oxide@amorphous cobalt boride nanocomposites with enhanced specific capacity for hybrid supercapacitors

Core–Shell Structured Carbon Nanofiber-Based Electrodes for High-Performance Supercapacitors

Chromium induced nickel oxides leads to extraordinary enhancement in the performance of aqueous hybrid supercapacitors

Thiol-functionalized conductive Co-MOF and its derivatives S-doped Co(OH)2 nanoflowers for high-performance supercapacitors

Development of 3D compound structures and highly wettable carbonate hydroxide electrodes for high-performance supercapacitors

Core-shell nanowires of NiCo<sub>2</sub>O<sub>4</sub>@-Co(OH)<sub>2</sub> on Ni foam with enhanced performances for supercapacitors