Effect of theoretical volume fraction (TVF) of reinforcements on Al5083/SiC and Al5083/ZrB 2 surface composites produced by friction stir processing
Nihat Kaya,Cemil Çetinkaya,Hakan Ada
DOI: https://doi.org/10.1016/j.matchemphys.2024.130012
IF: 4.778
2024-10-08
Materials Chemistry and Physics
Abstract:This study focuses on the effects of theoretical volume fraction (TVF) on the microstructure and mechanical properties of silicon carbide (SiC) and zirconium diboride (ZrB 2 ) ceramic reinforced Al5083 surface composites (SC). Al5083–H111 was used as the base material (BM), SiC and ZrB 2 were used as reinforcement materials, and TVFs were determined as 5, 10, 15, and 20 % for SCs produced by the friction stirring process (FSP). Macrostructure, microstructure, X-ray diffraction (XRD) analysis and mechanical properties such as microhardness, tensile strength (UTS), and wear behaviour were characterised. When the TVF and AVF values of SiC and ZrB 2 particles were compared, it was found that the AVFs were lower than the TVFs. Significant decreases in the changes in the SZ areas of SiC and ZrB 2 particle SCs were detected depending on the reinforcement size. In the time-dependent axial load graphs of SiC and ZrB 2 reinforced samples, load values ranging from 7800 to 8200 N were obtained and it was determined that these values were sufficient for friction heat, hydrostatic pressure, and plasticisation in FSP. As a result of mechanical characterisation processes, the microhardness values and wear rates of ZrB 2 reinforced SCs in the stir zone (SZ) were higher than SiC reinforced SCs. When the reinforcement particles were compared, it was observed that ZrB 2 reinforced SCs exhibited higher microhardness and wear resistance than SiC reinforced SCs. As a result of all tests and investigations, it was determined that the ideal TVFs were 15 % for SiC reinforced SCs and 5 % for ZrB 2 reinforced SCs. The microhardness value of ZrB 2 reinforced SC with 20 % TVF was 119.6 HV, while the UTS and volume loss values of ZrB 2 reinforced SC with 5 % TVF were found to be the highest values with 305.86 MPa and 1.83 mm 3 , respectively. Compared to BM, these values showed significant improvements in mechanical test results, especially in wear behavior. The results obtained showed an improvement of 55 % in microhardness, 3.3 % in UTS values, and 309 % in wear behavior.
materials science, multidisciplinary