Abstract:The MgAl layered hydrotalcites (MgAl-LDHs) precursors with submicron-scale were synthesized by introducing ethanol into hydrothermal synthesis method. The synthesis process parameters were optimized by orthogonal experiment, and then the composite metal oxide (MgAlOx) was obtained after the calcination process. The crystal phase, morphology and alkalinity of both hydrotalcite precursors and solid base oxides were characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and the temperature-programmed desorption of CO2(CO2-TPD), respecitively. Finally, the catalytic performance of MgAlOx was evaluated by the depolymerization test of calcium lignosulfonate. The products including solid, liquid, gas three phases, were analyzed by gel permeation chromatography (GPC), gas chromatography/mass spectrometry (GC-MS) and gas chromatography (GC). The results indicated that 140-230 nm of MgAl-LDHs were regulated by adding 15% (volume fraction) C2H5OH to the hydrothermal system, the optimal synthesis condition considered from relative crystallinity was n(Mg)/n(Al)=3, pH=12 and the temperature of 80 degrees C for 24 h. the MgAlOx obtained after the calcination of MgAl-LDHs at 600 degrees C for 6 h under air atmosphere. The optimal depolymerization of calcium lignosulfonate was 270 degrees C, 4 h, the addition of 65% (volume fraction) C2H5OH and m(MgAlOx)/m(CLS)=1/2. The gas-liquid-solid three-phase yield distribution was 4.50%, 58.30% and 37.20% under the above condition, the liquid yields increased by 13.30% with the addition of MgAlOx, the main components of liquid products were phenolics, aromatics, esters and others. Moreover, the selectivity of oxy-containing compounds was 79.05% (phenolics of 66.06%, esters of 12.99%). Fortunately, MgAlOx would also keep high reactivity and stability even after four cycles of reactions.

Fabrication of hierarchically porous MgO with high surface area and adjustable alkalinity for efficient transesterification synthesis of ethyl methyl carbonate

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

Ce/MgAl mixed oxides derived from hydrotalcite LDH precursors as highly efficient catalysts for ketonization of carboxylic acid

Excess soluble alkalis to prepare highly efficient MgO with relative low surface oxygen content applied in DMC synthesis

Influence of Acid-Base Properties of ZnMgAl-mixed Oxides for the Synthesis of 1-Methoxy-2-propanol

Formation of Ordered Mesoporous MgO with Tunable Pore Diameter and Its Application As Excellent Alkaline Catalyst in Baeyer−Villiger Oxidation

Efficient synthesis of ethylene carbonate via transesterification of ethylene glycol with dimethyl carbonate over Mg3Al1−xCexO composite oxide

Mg–Al Mixed Oxide Derived from Hydrotalcites Prepared Using the Solvent-Free Method: A Stable Acid–Base Bifunctional Catalyst for Continuous-Flow Transesterification of Dimethyl Carbonate and Ethanol

Preparation of MgO Nanosheets with Polar (111) Surfaces by Ligand Exchange and Esterification – Synthesis, Structure, and Application As Catalyst Support

An atom-economic reaction for synthesis of 1-phenoxy-2-propanol over Al2O3/MgO

Preparation of Shaped Magnesium Oxide/carbon Catalysts Using Rice Grains As an Exotemplate and Carbon Precursor

Preparation of High Specific Surface Area Mgo by A Gel-Templating Route

Synthesis of Dimethyl Carbonate via Transesterification of Ethylene Carbonate and Methanol over mesoporous KF‐loaded Mg‐Fe oxides

Protecting Mg-sites from hydration by embedding magnesium-aluminium layered double hydroxide in halloysite and using as pickering catalysts in Baeyer-Villiger oxidation

La‐Doped Mg‐Al Composite Oxides: Efficient Catalysts for the synthesis of Diethyl Carbonate via Transesterification of Ethylene Carbonate with Ethanol

Readily-fabricated supported MgO catalysts for efficient and green synthesis of diethyl carbonate from ethyl carbamate and ethanol

ZnxMg1‐xO Solid Solutions: Efficient Bifunctional Acid‐Base Catalyst for the synthesis of Methyl Ethyl Oxalate from Dimethyl Oxalate and Ethanol

Preparation and characterization of Mg-modified zirconias as catalysts for the direct synthesis of dimethyl carbonate (DMC)

Synthesis and characterization of magnesium oxide supported catalysts with a meso-macropore structure

Production of Oxygen-containing Compounds Catalytic from Depolymerization of Calcium Lignosulphonate by Submicron-scale MgAl Solid Base

Efficient Synthesis of Dimethyl Carbonate Via Transesterification of Ethylene Carbonate over A New Mesoporous Ceria Catalyst