Abstract:<p class="Para">Catalytic conversion of methanol to gasoline range hydrocarbons, especially aromatics was carried out in a fixed bed reactor over nano-crystal composite H-ZSM-5/11 zeolite synthesized by hydrothermal method. The metals of Zn, Cu, Ga and Ag as bimetallic Zn-Cu and Ga-Ag with different concentrations (3: 2, 5: 3) and (1:1, 3:2) respectively were selected for loading into the prepared zeolite catalysts. Direct synthesis method was used for incorporating metals. Prepared zeolites were characterized by XRD, SEM, TEM, N<sub>2</sub> adsorption-desorption, ICP-OES, NH<sub>3</sub>-TPD and FT-IR. After incorporation of metal species into the zeolites framework, the particles crystalline size was reduced, the intercrystalline porosity was increased, causing the formation of new moderate acid sites. The catalytic results illustrated that the incorporation of metal species enhanced the activity and catalyst stability in MTA reaction. BTX yield in ZSM-5/11 reached up at 23.5% to 30.4% and 25.88% with Zn-Cu-ZSM-5/11(1) and Ga-Ag-ZSM-5/11(1), respectively whereas heavier aromatics production reduced. Also, the comparison of catalysts with different metals content showed that due to improvement in structure and properties, low metal content zeolites have better performance in converting methanol to aromatics.</p><h3 class="Heading">Graphic abstract</h3>The catalytic conversion of methanol to the hydrocarbons, particularly aromatics, was investigated with bimetallic Zn-Cu-ZSM-5/11 and Ga-Ag-ZSM-5/11 catalysts. Incorporated metals replaced parts of the conventional acid sites and formed some new acid sites in the zeolites. The change in acidity and mesoporosity significantly improved aromatization reaction and catalyst stability <a href="https://media.springernature.com/original/springer-static/image/art%3A10.1007%2Fs12039-019-1684-8/MediaObjects/12039_2019_1684_Figa_HTML.png"><span class="u-screenreader-only">Open image in new window</span></a>

Conversion of Glycerol to Aromatics Over Hollow Hzsm-5 Based Catalyst: Effects of Metal Modification and Preparation Method

Enhanced performance of glycerol to aromatics over Sn-containing HZSM-5 zeolites

Effects Of Additives And Metals On Crystallization Of Nano-Sized Hzsm-5 Zeolite For Glycerol Aromatization

Shape Selectivity Conversion of Biomass Derived Glycerol to Aromatics over Hierarchical HZSM-5 Zeolites Prepared by Successive Steaming and Alkaline Leaching: Impact of Acid Properties and Pore Constraint

Aromatization of Methanol over La/Zn/HZSM-5 Catalysts

Tailoring the impact of synthetic strategies on the catalytic upgrading of crude glycerol to produce bio-based aromatics in hierarchical HZSM-5

Conversion of methanol to aromatics over ZSM-5/11 intergrowth Zeolites and bimetallic Zn-Cu-ZSM-5/11 and Ga-Ag-ZSM-5/11 catalysts prepared with direct synthesis method

Catalytic upgradation of crude glycerol to produce bio-based aromatics over hierarchical MFI zeolite: Effect of bimodal hierarchical porosity enhancement and porosity-acidity interaction

Synergy Effect Between Hierarchical Structured and Sn-modified H[Sn, Al]ZSM-5 Zeolites on the Catalysts for Glycerol Aromatization

Sn and Zn Modified Hzsm-5 for One-Step Catalytic Upgrading of Glycerol to Value-Added Aromatics: Synergistic Combination of Impregnated Sn Particles, Ald Introduced Zno Film and Hzsm-5 Zeolite

Aromatization of mixed C4 hydrocarbons over ZnNi/HZSM-5 catalyst

Catalytic Cracking of Fatty Acid Methyl Esters for the Production of Green Aromatics Using Zn-Modified HZSM-5 Catalysts

The Effect of Hierarchical Pore Architecture on One-Step Catalytic Aromatization of Glycerol: Reaction Routes and Catalytic Performances

Preparation of Nano-Sized HZSM-5 Zeolite with Sodium Alginate for Glycerol Aromatization

A Highly Active and Stable Zn@C/HZSM-5 Catalyst Using Zn@C Derived from ZIF-8 As a Template for Conversion of Glycerol to Aromatics

Modified ZSM-5 Zeolite for Conversion of LPG to Aromatics

Utilization of Metal-Functionalized ZSM-5 for Methanol and Low-Carbon Hydrocarbon Coupling Aromatization

In Situ Synthesis of Metal-Containing ZSM-5 and Its Catalytic Performance in Aromatization of Methanol.

Selective Conversion of Syngas to Aromatics over Metal Oxide/hzsm-5 Catalyst by Matching the Activity Between CO Hydrogenation and Aromatization

The catalytic properties evolution of HZSM-5 in the conversion of methanol to gasoline

The Aromatization Properties of Nano-HZSM-5 Catalyst