Abstract:Objectives This study investigated effects of the different emittance-mode protocols from three light curing units (LCUs): (i) a Laser (Monet); (ii) a quad-wave (PinkWave); (iii) a conventional LED (Elipar S10) on the temperature rise (ΔT) and degree of conversion (DC) when photo-curing fast or conventional bulk-fill resin-based composites (RBC). The aim was to correlate ΔT and DC, and the radiant exposure delivered to RBC specimens. Methods A 3D-printed resin mold of 4 mm depth was filled with two bulk-fill RBCs: Tetric PowerFill® ( fast photo-polymerised composite) ( TPF ) or Tetric EvoCeram® Bulk-Fill ( EVO ). Three LCUs were used: (i) Monet laser for 1 s and 3 s ( MONET-1 s, MONET-3 s ); (ii) PinkWave quad-wave used for 3 s in Boost mode ( PW-3 s ) and for 20 s in standard mode ( PW-20 s ); (iii) Elipar S10 for 5 s ( S10–5 s ) and for 20 s in standard mode ( S10–20 s ). 2-dimensional temperature maps were obtained before, during and for 60 s after the LCU had turned off using a thermal imaging camera. Thermal changes were analysed at five depths: (0, 1, 2, 3, and 4 mm from the top surface of the RBC). The maximum temperature rise ( T max ) and the mean temperature rise ( ΔT ) were determined. Cylindrical-shaped specimens were prepared from each material using a stainless-steel split mold (4 × 4 mm) and light-cured with the same protocols. The DC was measured for 120 s and at 1 h after LCU had turned off using Fourier Transform Infrared Spectroscopy (FTIR). Data were analysed using Three-way ANOVA, One-way ANOVA, independent t-tests, and Tukey post-hoc tests (p < 0.05). Results Radiant exposures delivered by the various irradiation protocols were between 4.5–30.3 J/cm 2 . Short exposure times from MONET-1 s and PW-3 s delivered the lowest radiant exposures (4.5 and 5.2 J/cm 2 , respectively) and produced the lowest ΔT and DC. The longer exposure times in the standard modes of PW-20 s, S10–20 s, and MONET-3 s produced the highest T max , ΔT, and DC for both composites. The ΔT range among composites at different depths varied significantly (31.7–49.9 °C). DC of TPF ranged between 30–65% and in EVO between 15.3–56%. TPF had higher T max, ΔT for all depths and DC compared to EVO, across the LCU protocols (p < 0.05), except for PW-20 s and MONET-3 s. The coronal part of the restorations (1–2 mm) had the highest ΔT. There was a positive correlation between ΔT and DC at 4-mm depth after 120 s Significance Longer, or standard, exposure times of the LCUs delivered greater radiant exposures and had higher DC and ΔT compared to shorter or high-irradiance protocols. The fast photo-polymerised RBC had comparatively superior thermal and conversion outcomes when it received a high irradiance for a short time (1–5 s) compared to the conventional Bulk-Fill RBC.

Influence of light exposure techniques on in vitro pulp temperature rise during bulk fill composite Class I restorations

Composite Cure and Pulp-Cell Cytotoxicity Associated with LED Curing Lights.

Effect of composite temperature on in vitro intrapulpal temperature rise

Pulpal Temperature Variances During Step-by-step Adhesive Restorative Procedure Using Three Different High-irradiance Light-curing Units

Effect of Rapid High-Intensity Light-Curing on Increasing Transdentinal Temperature and Cell Viability: An In Vitro Study

Evaluation of pulp chamber temperature during cementation with the preheated composite resin technique

Temperature change in pulp chamber of primary teeth during curing of coloured compomers: an in vitro study using pulpal blood microcirculation model

The role of protective liners and glass ionomer in managing pulp temperature during light curing

Temperature change of the pulpal floor and restoration with preheated bis-GMA free and containing resin composite (a randomized clinical trial)

Evaluation of temperature increase during in-office bleaching

The Effect of Light-emitting Diode Light Intensities and Duration of Cure on Pulpal Wall Temperature among Different Classes of Teeth

Effect of Radiant Exposure on the Physical and Mechanical Properties of 10 Flowable and High-viscosity Bulk-fill Resin Composites

The Effects of Intensity, Exposure Time, and Distance of Polymerization Light on Vickers Microhardness and Temperature Rise of Conventional Resin-Based Composite

Thermography and conversion of fast-cure composite photocured with quad-wave and laser curing lights compared to a conventional curing light

Effect of translucency and absorbance of composite on temperature change during photopolymerization

The effect of light curing intensity on bulk-fill composite resins: heat generation and chemomechanical properties

Intra-pulpal and subsurface temperature rise during tooth irradiation with 808 nm diode laser: an in vitro study

Effects of Light Attenuation through Dental Tissues on Cure Depth of Composite Resins

Effect of temperature and humidity on post-gel shrinkage, cusp deformation, bond strength and shrinkage stress - Construction of a chamber to simulate the oral environment

Effect of short LED lamp exposure on wear resistance, residual monomer and degree of conversion for Filtek Z250 and Tetric EvoCeram composites

Diversity of short-term DC outcomes in bulk-fill RBCs subjected to a 3 s high-irradiance protocol