Ionic liquid-assisted production of high-porosity biochar with more surface functional groups: Taking cellulose as attacking target
Fan Yang,Xiuping Zuo,Haorong Yang,Qiang Ke,Yuandong Huang,Xinde Cao,Ling Zhao
DOI: https://doi.org/10.1016/j.cej.2021.133811
IF: 15.1
2022-04-01
Chemical Engineering Journal
Abstract:Biochar has been widely used as a multifunctional environmental material, mainly attributing to its porous structure and O-containing functional groups. However, it is hard to simultaneously improve these two properties, because pyrolysis at high temperature (600–700 °C) usually causes loss of functional groups while low temperature (300–400 °C) is adverse to form porous structure. Ionic liquid (IL) is an organic solvent, which is regarded to have catalysis on biomass during pyrolysis. In this study, a representative IL, 1-butyl-2,3-dimethylimidazolium triflate was selected to co-pyrolysis with wastepaper, and a biochar with high-porosity and more functional groups was produced at low temperature (350 °C). With incorporation of IL, the wastepaper biochar’s surface area and pore volume were increased from 19.8 to 52.8 m2 g−1 and from 0.033 to 0.174 cm3 g−1, respectively. Meanwhile, more O-containing functional groups were retained. In order to reveal the mechanisms, cellulose and lignin, as two model main compositions of wastepaper, were mixed with IL respectively to produce biochar. It was found that during thermal process, IL preferred to attack cellulose rather than lignin. Before 250 °C, IL induced cellulose cleaving to monosaccharides, including levoglucosan, furanoglucose and monocyclic furfural; between 250 °C and 300 °C, IL promoted monosaccharides dehydration by reducing dehydration activation energy, leading to a decrease of decomposition temperature. Adsorption experiments showed that this IL-modified biochar had a significantly higher Pb adsorbing capacity (99.4%) than the routine biochar (25.7%). This study provides a simple method to produce high-porosity biochar with more O-containing functional groups, which would maximize and broaden its environmental application.
engineering, chemical, environmental