Abstract:Biomimicking the chemical, mechanical, and topographical properties of bone on an implant model is crucial to obtain rapid and effective osteointegration, especially for the large-area fractures of the skeletal system. Titanium-based biomaterials are more frequently preferred in clinical use in such cases and coating these materials with oxide layers having chemical/nanotopographic properties to enhance osteointegration and implantation success rates has been studied for a long time. The objective of this study is to examine the high and rapid mineralization potential of anodized aluminum oxide (AAO) coated and atomic layer deposition (ALD)-alumina coated titanium substrates on large deformation areas with difficult spontaneous healing. AAO-coated titanium (AAO@Ti) substrates were fabricated via anodization technique in different electrolytes and their osteogenic potential was analyzed by comparing them to the bare titanium surface as a control. In order to investigate the effect of the ionic characters gained by the surfaces through anodization, the oxidized nanotopographic substrates were additionally coated with an ultrathin alumina layer via ALD (ALD@AAO@Ti), which is a sensitive and conformal coating vapor deposition technique. Besides, a bare titanium sample was also coated with pure alumina by ALD (ALD@Ti) to investigate the effect of nanoscale surface morphology. XPS analysis after ALD coating showed that the ionic character of each surface fabricated by anodization was successfully suppressed. In vitro studies demonstrated that, among the substrates investigated, the mineralization capacity of MG-63 osteosarcoma cells were highest when incubated on ALD-treated and bare AAO@Ti samples that were anodized in phosphoric acid (H3PO4_AAO@Ti and ALD@H3PO4_AAO@Ti). Mineralization on these substrates also increased consistently beginning from day 2 to day 21. Moreover, immunocytochemistry for osteopontin (OPN) demonstrated the highest expression for ALD@H3PO4_AAO@Ti, followed by the H3PO4_AAO@Ti sample. Consequently, it was observed that, although ALD treatment improves cellular characteristics on all samples, effective mineralization requires more than a simple ALD coating or the presence of a nanostructured topography. Overall, ALD@H3PO4_AAO@Ti substrates can be considered as an implant alternative with its enhanced osteogenic differentiation potential and rapid mineralization capacity.

Fabrication of Aligned Alanine Functionalized Hydroxyapatite Nanorods Embedded in Electrospun Gelatin Scaffolds as a Coating Material for Titanium Bone Implant Application

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Hydroxyapatite Nanoparticle-Coated 3D-Printed Porous Ti6Al4V and CoCrMo Alloy Scaffolds and Their Biocompatibility to Human Osteoblasts

Fabrication of anodic and atomic layer deposition-alumina coated titanium implants for effective osteointegration applications

A Bioinspired Gelatin–Amorphous Calcium Phosphate Coating on Titanium Implant for Bone Regeneration (Adv. Healthcare Mater. 20/2023)

Greater osteoblast and mesenchymal stem cell adhesion and proliferation on titanium with hydrothermally treated nanocrystalline hydroxyapatite/magnetically treated carbon nanotubes

Nano-hydroxyapatite Crystal Formation Based on Calcified TiO2 Nanotube Arrays

Hydrothermal growth of biomimetic calcium phosphate network structure on titanium surface for biomedical application

Bone-like growth of hydroxyapatite in the biomimetic coating of Ti-6Al-4V alloy pretreated with protein at 25 °C

Electrospray deposition of nanohydroxyapatite coatings: A strategy to mimic bone apatite mineral

Fabrication and characterization of biomimetic hydroxyapatite thin films for bone implants by direct ablation of a biogenic source

Fabrication of Mineralized Electrospun PLGA and PLGA/gelatin Nanofibers and Their Potential in Bone Tissue Engineering

Polydopamine Coating Promotes Early Osteogenesis in 3D Printing Porous Ti6Al4V Scaffolds.

Hydroxyapatite based on Abalone Mussel Shells Coating on Titanium Alloy using Electrophoretic Deposition Dip Coating as a Bone Implant Candidate

Optimizing alkaline hydrothermal treatment for biomimetic smart metallic orthopedic and dental implants

Biocompatible Nanotube‐Strontium/polydopamine‐arginine–glycine–aspartic Acid Coating on Ti6Al4V Enhances Osteogenic Properties for Biomedical Applications

In Vitro Evaluation of Biologically Derived Hydroxyapatite Coatings Manufactured by High Velocity Suspension Spraying

Improved Biocompatible, Flexible Mesh Composites for Implant Applications via Hydroxyapatite Coating with Potential for 3-Dimensional Extracellular Matrix Network and Bone Regeneration

Calcium alginate template-mineral substituted hydroxyapatite hydrogel coated titanium implant for tibia bone regeneration

Electrohydrodynamic Deposition of Nanotitanium Doped Hydroxyapatite Coating for Medical and Dental Applications