Effects of film thickness on crystal structure, surface topography, optical, and photoelectric properties of Ga2O3 thin film based solar blind photodetectors

Zheng-Nan Li,Zhao-Cai Wang,Chen Li,Bao-Lin Lu,Wei Yan,Chen-Long Huang,Tao Zhang,Yin-Hong Luo,Ren-Kui Zheng
DOI: https://doi.org/10.1088/1402-4896/ad0335
2023-10-15
Physica Scripta
Abstract:β-Ga2O3 epitaxial thin films with different thicknesses were grown on Al2O3(0001) substrates by the pulse laser deposition technology. Full width at half maximum of XRD rocking curve, grain size, surface roughness, and optical absorbance (200-300 nm) of the β-Ga2O3 films increase with increasing film thickness. In addition, with increasing film thickness, the adsorption edge presents a red-shift phenomenon, which is accompanied by a slight decrease in the optical band gap (Eg). The metal-semiconductor-metal type photodetector made with the 401-nm β-Ga2O3 film shows the maximal photocurrent (1.06 μA@ 10 V), photo-to-dark current ratio (6.96×10 4), responsivity (90 mA/W), and detectivity (0.5×10 11 Jones) under 254-nm UV light illumination with a light intensity of 98.4 μW/cm2. Moreover, the 401-nm photodetector displays a small rise time of 0.111/0.561 s and a decay time of 0.046/0.047 s as well as a good stability and repeatability. These findings provide useful reference for the fabrication of β-Ga2O3 film based solar blind ultraviolet photodetectors.
physics, multidisciplinary
What problem does this paper attempt to address?