Rich Alkali Ions Preintercalated Vanadium Oxides for Durable and Fast Zinc-Ion Storage
Guoqun Zhang,Tao Wu,He Zhou,Hongrun Jin,Kaisi Liu,Yongxin Luo,Haifeng Jiang,Kevin Huang,Liang Huang,Jun Zhou
DOI: https://doi.org/10.1021/acsenergylett.1c00625
IF: 22
2021-05-12
ACS Energy Letters
Abstract:Vanadium oxides are a promising class of cathode materials for rechargeable aqueous zinc-ion batteries (ZIBs). However, the intrinsically low electrical conductivity and unstable structure of vanadium materials often lead to fast performance degradation. In this work, we report on potassium-rich preintercalated vanadium oxide (K<sub>1.1</sub>V<sub>3</sub>O<sub>8</sub>) as a high-performance cathode material for ZIBs. The K<sub>1.1</sub>V<sub>3</sub>O<sub>8</sub> cathode exhibits a high specific capacity of 386 mAh g<sup>–1</sup> at 0.1 A g<sup>–1</sup> and good long-term cycling stability with a capacity retention of 114.9% (180.7 mAh g<sup>–1</sup>) after 10 000 cycles at 10 A g<sup>–1</sup>. The DFT calculations reveal a low Zn diffusion barrier and low Bader charge of K in K<sub>1.1</sub>V<sub>3</sub>O<sub>8</sub>, which are responsible for its good rate capability and high storage performance. The demonstration approach of maximizing ZIB performance proves to be an effective way to design promising cathode materials for ZIBs by regulating the appropriate preintercalation metal ions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsenergylett.1c00625?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsenergylett.1c00625</a>.Kinetics analysis of the energy storage reaction; DFT computational methods; The electrochemical reactions of KVO cathode; Crystal structures of active materials (Figure S1); The FTIR spectrum of LiVO, NaVO, and KVO (Figure S2); XRD, SEM, HRTEM and STEM of LiVO (Figure S3); XRD, SEM, HRTEM and STEM of NaVO (Figure S4); XPS of LiVO and NaVO (Figure S5); CV curves and GCD of LiVO and NaVO (Figure S6); CV curves and GCD of CNT (Figure S7); The Nyquist plots of LiVO, NaVO and KVO based electrodes before and after cycling in two electrode configuration (Figure S8–S9); The cycling performance of LiVO, NaVO and KVO electrodes (Figure S10); The contribution ratio of capacitive process calculated from CV curves of KVO (Figure S11); The Nyquist plots of LiVO, NaVO and KVO in the three-electrode configuration (Figure S12); The electrochemical performance of KV<sub>3</sub>O<sub>8</sub> electrode (Figure S13); TEM image, HRTEM image with SAED pattern, and STEM elemental mapping of KVO discharged to 0.2 V (Figure S14); The intercalation process of Zn<sup>2+</sup> into the V–O interlayer spacing of KVO (Figure S15); The intercalation process of Zn<sup>2+</sup> into the V–O interlayer spacing of LiVO and NaVO (Figure S16); The intercalation process of H<sup>+</sup> into the V–O interlayer spacing of LiVO, NaVO and KVO (Figure S17) (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.1c00625/suppl_file/nz1c00625_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology,energy & fuels,electrochemistry