Effects of Activator Types on Degradation Mechanisms of Metakaolin Geopolymer Mortars Exposed to High Temperature
Yajun Zhang,Dongming Yan,Nv Han,Yu Ao,Shikun Chen,Hailong Ye,Hamed Fazli,Tian-Nan Ye
DOI: https://doi.org/10.1061/(ASCE)MT.1943-5533.0003457
IF: 3.2
2020-01-01
Journal of Materials in Civil Engineering
Abstract:In this study, we investigated the degradation process of metakaolin-based geopolymers exposed to high temperatures up to 1,000 degrees C. The changes in mechanical properties, microstructure, and phase assemblage of the samples were studied, and the results demonstrated that at high temperatures the activator type [i.e., Na2SiO3/NaOH (Na/Na) and Na2SiO3/KOH (Na/K) solution] affected the degradation mechanisms of geopolymer mortars. (Na,K)-based geopolymer specimens demonstrated better thermal resistance at temperatures above 200 degrees C. This was evident from the higher compressive strength, lower porosity, and less cracking tendency of this mixture. Compared to (Na,K)-based geopolymers, more mass loss may result in considerable drying shrinkage of (Na,Na)-based counterparts, which would further lead to the occurrence and development of cracks at similar to 200 degrees C. Above 200 degrees C, the degradation of the mechanical properties of geopolymers could be attributed to crack development and degradation of material properties. Furthermore, compared to their (Na-Na)-based counterparts, (Na-K)-based geopolymers achieved improved chemical stability and did not form new crystalline phases above 1,000 degrees C. Moreover, higher temperature exposure (1,000 degrees C) led to significant sintering of geopolymers, forming a dense and homogeneous matrix and, as a result, improved mechanical properties of specimens. Overall, it showed that when specimens were exposed to different high temperatures, the mutual promoted effects between Na+ and K+ in geopolymers played a significant role in crack development, sintering, and new crystallization formation in the specimens. (c) 2020 American Society of Civil Engineers.