Structure–property relationships for quenched and tempered flanges made to ASTM A350 LF2 specification
B. Mintz,J. Kolahi-aval,M. Saggese
DOI: https://doi.org/10.1179/mst.1988.4.7.603
IF: 1.8
1988-07-01
Materials Science and Technology
Abstract:The structure–property relationships for quenched and tempered flanges made to the ASTM A350 LF2 specification have been determined. Samples from Al containing and Al free forged flanges have been heated to temperatures in the range 900–1000°C to produce a wide range in γ grain size and quenched in oil or iced water to produce a variety of commercially obtainable microstructures from fine grained ferrite–pearlite to fully bainitic. After quenching, the samples were tempered at 600°C, and the Charpy V-notch impact values at −46°C and room temperature hardness values were obtained. Raising the quenching temperature reduced the impact energy values and increased the hardness. Increasing the cooling rate also increased hardness, but there was little change in impact behaviour. Impact behaviour was found to be mainly dependent on the γ grain size: the coarser the grain size, i.e. the higher the quench temperature, the lower the impact value. The facet size was also found to be related to γ grain size, indicating that the high angle grain boundaries, i.e. γ, bainite colony, and ferrite boundaries, were the main obstacles to crack propagation. Increasing the cooling rate from the austenitising temperature increased hardness without significantly affecting the impact behaviour. It is believed that the expected deterioration in impact behaviour associated with an increase in hardness was offset by a refinement of the carbides and the removal of the long carbides situated at the interlath ferrite boundaries. The impact energy in joules at −46°C was given by the equation: impact energy absorbed at −46°C=82+18·6d−1/2−0·8H+0·05CR, where d is austenite grain size in millimetres, H is hardness HV10, and CR is cooling rate in K min−. To meet the ASTM A350 LF2 impact requirement, the γ grain size should be below 40 μm, and this necessitates a grain refining addition. MST/771
materials science, multidisciplinary,metallurgy & metallurgical engineering