Tribological Properties of PTFE/PI-PAI Coatings with Different Thickness under Different Lubricating Medium and Substrate
Chuankun Tu,Jun Cao,Minghao Zhu,Peiqing Ye,Jingshan Xie
DOI: https://doi.org/10.11933/j.issn.1007-9289.20230313001
2024-01-01
China surface engineering
Abstract:As ships are attacked by shells or come in contact with reefs, the engine compartment experiences extreme working conditions, such as oil lubrication, seawater corrosion, and even dry sliding wear. To improve the tribological performance of a ship's engine bearing under extreme working conditions and ensure the smooth return of the ship after damage, we designed a polymer coating consisting of PTFE / PI-PAI and ZrO2. Three different coatings of different thicknesses were prepared using liquid spraying on the surfaces of the A370 aluminum alloy and CuPb22Sn2.5 copper alloy. The tribological performance of these coatings with different lubricating media was studied. The performance of the coatings was evaluated based on their physical phase composition, microstructure morphology, element distribution, bond strength between the coating and substrate, nano-hardness, Young's modulus, and frictional wear behavior. The tribological properties of the coatings were investigated using various lubricating media. The results showed that the physical phase and solid distribution of the coatings were not influenced by variations in the coating thickness. The hardness and elastic moduli of the coatings decreased with increasing coating thickness, and the hardness of the coating on the copper alloy substrate was higher than that on the aluminum alloy substrate. The thicker the coating, the less supported the action of the hard substrate. Compared with coating under 20 mu m thickness, the supporting effect of coating under 50 mu m thickness on the aluminum alloy and copper alloy substrate was increased by 1 297.78% and 1 767.98%, respectively. The coefficients of friction (CoFs) and wear rates of the coatings on the copper alloy substrate under oil-lubricated conditions were lower than those on the aluminum alloy substrate. The wear rate of the coatings decreased with increasing coating thickness. The maximum variation in the CoFs of the coatings with different thicknesses on different substrates was only 3.33%. Oil lubrication is a key factor resulting in these frictional properties. Abrasive wear and significant plowing were observed under corrosive seawater conditions. The CoFs of the coatings on the copper alloy substrate were higher than those of the coatings on the aluminum alloy substrate. Seawater corrosion and the effect of seawater scouring during high-frequency reciprocating frictional movements were the main factors influencing frictional performance. The wear mechanism of the coating under dry sliding was primarily adhesive wear. The coating entered stable wear at 600 s under dry sliding wear, which occurred later than under seawater conditions. Adhesive wear is the main reason for this observation. The hardness of the coating was influenced by the supporting action of the substrate. The tribological performance of the copper alloy coating was better than that of the aluminum alloy coating. The pinch action from the high-frequency reciprocating motion of the hard grinding ball to the soft coating on the hard substrate and the contact pressure were the main factors. The marine engine bearing had the best tribological performance under the coating with 30 mu m thickness prepared on the copper alloy substrate. Compared with the CoF of the copper substrate, the CoFs of the coatings under dry sliding wear and seawater decreased by 72.16% and 36.07%, respectively. The tribological performance of marine engine bearings under extreme conditions can be improved using this coating. In this study, the support mechanism from the substrate to self-lubricating coatings with different thicknesses was elucidated. The tribological performance of the coating under extreme conditions was analyzed, and the optimum coating thickness on a marine engine bearing was determined.