A thin composite coating for threads protection: Synergistic effect of modified MoS2 and F-CeO2 nanoflakes

Yuting Wei,Yongli Sun,Huaiyuan Wang

DOI: https://doi.org/10.1016/j.cej.2023.145667

IF: 15.1

2023-10-01

Chemical Engineering Journal

Abstract:Threads are widely applied in every aspect, but solving the existing problems of their corrosion and gluing is still highly challenging. Herein, the thin polysiloxane composite coating endowed with versatile properties of anti-corrosion and friction reduction was successfully prepared through introducing MoS2 modified by KH560 (m-MoS2) and F-doped CeO2 (F-CeO2) nanoflakes. F-CeO2 nanoflakes, obtained via the solvothermal method, play the dominant role of resisting corrosion because the doped fluorine can promote to form the passivation layer; and the lamellar structure of m-MoS2 and F-CeO2 nanoflakes helps to improve the corrosion resistance. Besides, lubricative m-MoS2, achieved through the reflux method, decreases the friction coefficient greatly when F-CeO2 nanoflakes are regarded as a plus. Specifically, the impedance at 0.01 Hz of the optimal coating filled with m-MoS2 and F-CeO2 nanoflakes remained at 4.39 × 1010 Ω·cm2 after the 70-d immersion in 3.5 wt% NaCl solution, much higher than that of the coating without any filler (1.44 × 105 Ω·cm2). And the average friction coefficient and wear rate of the coating respectively reduced by 41.81% and 54.31% for introducing the effective nanofillers. For the synergism of m-MoS2 and F-CeO2 nanoflakes, the comprehensive performance of the target coating enhanced substantially, meeting the requirements of the protective coating for threads.

engineering, chemical, environmental