Abstract:In machining, heat concentration is generated at the surface contact between the tool and workpiece. This is the effect of hard frictions at the shear cutting plane to remove hard and brittle materials. The highly adhesive behavior of aluminum alloy 6061-T6 is more severe in higher cutting temperature, which may affect tool failures such as flank wear, tool chip and built-up edge, particularly on the edge of cutting inserts during the process. As a result, this may lead to the rough surface and low-dimensional accuracy of the machined parts. Realizing that metal-cutting industry players are demanding high-quality products with better surface finish and dimensional accuracy led to this study. Aluminum alloy 6061-T6 is a standard alloy used in automotive, aerospace and food packaging due to good hardness, high strength-to-weight ratio, resistance to corrosion and weldability. In order to address this problem, a newly developed metal working fluid which is SiO2-Al2O3-ZrO2 tri-hybrid nanofluid is applied in the cutting zone to achieve a good surface finish of the machined parts and lowering the cutting temperature. This study is the first attempt to enhance machining performance, particularly at high-speed machining, by employing a combination of tri-hybrid nanofluids and a minimum quantity lubricant technique. Industrial standards include uncoated tungsten carbide and CVD TiCN-Al2O3 carbide used during machining of aluminum alloy 6061-T6. The minimum quantity lubricant method is an alternative in supplying the lubricant into the machining zone due to flood machining and conventional fluid possess safety, health, economic and environmental effects. In this study, the experimental data were analyzed statistically using analysis of variance and response surface methodology. The responses studied were reduced significantly when tri-hybrid nanoparticles present at the cutting interface with higher MQL flow rate and concentration. There are two-factor interactions which are significant to the responses studied. Therefore, the combinations of MQL and excellent tri-hybrid nanofluids characteristics have enhanced between 16 and 76% of surface roughness and the cutting temperature, respectively, which is very promising in the future.

The Effect of Cutting Parameters on Surface Quality and Corrosion Resistance of Micro-machined Surfaces of 7075 Aluminum Alloy

Effect of cutting parameters on the microstructure evolution and damage mechanism of 7075-T6 aluminum alloy in micro cutting

Corrosion mechanism and machinability of 7075‐T6 aluminum alloy in high‐speed cutting: With and without cryogenic treatment

Effect of cutting parameters on the corrosion resistance of 7A04 aluminum alloy in high speed cutting

Study on the Micro-cutting Mechanism of 7075 Aluminum Alloy with Pre-fabricated Surface Microtextures

Investigation on the damage mechanism of micro-cutting surface layer of aluminum alloy 7075 with different heat treatment processes

Electrochemical corrosion behavior of 7075 aluminum alloy with different ultrasonic surface rolling microstructures

Prediction of surface roughness and optimization of process parameters for efficient cutting of aluminum alloy

Experimental Investigation on Machinability of Aluminum Alloy during Dry Micro Cutting Process Using Helical Micro End Mills with Micro Textures

CHARACTERIZATION OF SURFACE, SUBSURFACE DAMAGE AND THEIR EFFECT ON FATIGUE LIFE AFTER MACHINING OF AEROSPACE-GRADE ALUMINUM ALLOY (Al 6082-T6)

Research on surface integrity and its influencing factors in the high-speed cutting of typical aluminum/titanium/nickel alloys: a review

Study on the Orthogonal Cutting Process of Al7050T7451 with Uncoated and Coated Tools

Residual stresses and surface damage when micromachining 6061-T6 aluminum alloy

Review of improvement of machinability and surface integrity in machining on aluminum alloys

Effect of End Milling Process Parameters and Corrosion Behaviour of ZE41A Magnesium Alloy using Taguchi Based GRA

Effect of Heat Treatment Process on the Surface Integrity of 7A04 Aluminum Alloy

Effects of SiO2-Al2O3-ZrO2 Tri-hybrid Nanofluids on Surface Roughness and Cutting Temperature in End Milling Process of Aluminum Alloy 6061-T6 Using Uncoated and Coated Cutting Inserts with Minimal Quantity Lubricant Method

Correlation between Microstructural Properties and Electric Parameters of Micro-Arc Oxidation Coatings on 5052 Aluminum Alloys with Improving Wear and Corrosion Resistance

Multiparameter signal-to-noise ratio optimization for end milling cutting conditions of aluminium alloy 5083

Study on the Influence of Surface Temperature Field of Aluminum Alloy Etched by Laser Water Jet Composite Machining

Effect of Surface Roughness Induced by Milling Operation on the Corrosion Behavior of Magnesium Alloys