A novel strategy to enhance the desalination stability of FAS (fluoroalkylsilane)-modified ceramic membranes via constructing a porous SiO2@PDMS (polydimethylsiloxane) protective layer on their top

Xue Dai,Qi Wei,Yali Wang,Qunyan Li,Suping Cui,Zuoren Nie
DOI: https://doi.org/10.1016/j.cej.2022.134757
IF: 15.1
2022-05-01
Chemical Engineering Journal
Abstract:The production of freshwater by desalination has great significance. Membrane distillation (MD) is considered as a promising technique for desalination. As a popular candidate for MD desalination, FAS (fluoroalkylsilane)-modified ceramic membrane suffers from insufficient stability, such as membrane wetting and decline of salt rejection during long-term operation, because of the degradation of hydrophobicity. In the present work, a novel strategy is proposed to enhance the long-term desalination stability of FAS-modified cordierite ceramic membranes by constructing a porous SiO2@PDMS (polydimethylsiloxane) protective layer on their tops to obtain a robust hydrophobic property. The results show that such a layer can be successfully fabricated by a two-step spraying method with hydrosoluble NaCl particles as templates. The incorporation of SiO2 nanoparticles into PDMS generates a loose and porous structure in the layer and renders an enhanced hydrophobicity. At a SiO2/PDMS mass ratio of 0.30, the membranes exhibit a notable resistance to both mechanical abrasion and chemical corrosion. The dissolution of NaCl templates leaves behind cavities within the layer, which prevents the SiO2/PDMS species from blocking the membrane pores and thereby helps to reduce the vapor transport resistance. These membranes are highly stable upon long-term desalination (>300 h) and can preserve a stable water flux of 8.10 kg/m2h and a salt rejection close to 100% under the following conditions: a feed temperature of 80 °C, a NaCl concentration of 3.5 wt% and a feed flow rate of 300 mL/min. The SiO2@PDMS layer is responsible for the outstanding desalination stability since it prevents membrane wetting by reducing the direct contact of the reflux feed solution to the underlying cordierite ceramic membranes.
engineering, chemical, environmental
What problem does this paper attempt to address?