Stress-modulated optimization of polymorphic phase transition in Li-doped (K,Na)NbO 3

Neamul H. Khansur,Alexander Martin,Kevin Riess,Hiroshi Nishiyama,Keiichi Hatano,Ke Wang,Jing-Feng Li,Ken-ichi Kakimoto,Kyle G. Webber

DOI: https://doi.org/10.1063/5.0016072

IF: 4

2020-07-20

Applied Physics Letters

Abstract:The effect of uniaxial compressive stress on the crystal structure of a 6 mol. % Li-doped (K,Na)NbO₃ (LKNN6a) ceramic was investigated using <i>in situ</i> synchrotron X-ray diffraction, revealing the stress-induced relative change in monoclinic <i>Pm</i> and tetragonal <i>P</i>4<i>mm</i> phases. As such, stress-induced phase transformations, in addition to the lattice deformation and domain switching, are the contributing factors for the observed macroscopic mechanical behavior of LKNN6a. The <i>in situ</i> stress-dependent diffraction data also demonstrates a method to mechanically modulate the polymorphic phase transition temperature (<i>T</i>_PPT) to a higher temperature, as observed by the temperature-dependent permittivity measurements under a constant bias stress. The external uniaxial compressive stress increases the stability of the lower symmetry monoclinic phase, shifting <i>T</i>_PPT to a higher temperature by 60 °C for the maximum uniaxial compressive stress of 300 MPa in the studied composition. Importantly, the stress-induced stabilization of the room-temperature ferroelectric phase can be useful to optimize the phase transition region, as well as increase the temperature stability of lead-free KNN.

physics, applied