Fabrication of flame retardant lyocell fibers based on carboxymethylation and aluminum ion chelation

Xun Guo,Yang Wang,Yuanlin Ren,Xiaohui Liu
DOI: https://doi.org/10.1007/s10570-021-03931-6
IF: 6.123
2021-05-20
Cellulose
Abstract:How to improve the flame retardancy of lyocell fibers has become an important issue in textile industry. Herein, lyocell fibers were firstly undergone etherification reaction between sodium chloroacetate and the hydroxyl groups of lyocell fibers to obtain carboxymethylated lyocell fibers (CM-lyocell), then the sodium ions of CM-lyocell were replaced by aluminum ions, and the flame retardant lyocell fibers (FR-lyocell) were prepared. Compared with lyocell fibers, the degradation temperature of FR-lyocell decreased by about 80 °C, and the char residue in nitrogen increased from 15.1 to 31.8 wt% at 800 °C. Importantly, the limiting oxygen index (LOI) value of FR-lyocell fabric was increased from 17.2 to 26.4%. Besides, the peak of heat release rate (PHRR) and total heat release (THR) of FR-lyocell had 77.4% and 76.3% reduction, respectively. The FR-lyocell can generate a highly graphitized char layer and release more water at high temperatures, which are beneficial to improving the flame retardancy of lyocell fibers. Moreover, the tensile test showed that the tensile strength of FR-lyocell decreased from 3.95 to 3.08 cN/dtex with a 22% reduction, showing good strength retention.
materials science, textiles,polymer science, paper & wood
What problem does this paper attempt to address?
The paper aims to address the flame retardancy issue of lyocell fibers in the textile industry. Specifically, the study involves etherification of lyocell fibers, followed by replacing the sodium ions in the resulting carboxymethyl lyocell (CM-lyocell) with aluminum ions, ultimately producing flame-retardant lyocell fibers (FR-lyocell). The paper details this process and verifies the flame-retardant properties and mechanisms of the new fibers through various characterization methods, such as thermogravimetric analysis, combustion tests, and microscale combustion calorimetry. The research results indicate that compared to the original lyocell fibers, FR-lyocell fibers not only increase the limiting oxygen index (LOI) but also significantly reduce the heat release rate and total heat release, demonstrating good flame-retardant effects. Additionally, although their tensile strength decreases, they still maintain a good strength retention rate.