The combined effect of impregnated rollers configuration and glass fibers surface modification on the properties of continuous glass fibers reinforced polypropylene prepreg composites

Jianpeng Fang,Ling Zhang,Chunzhong Li

DOI: https://doi.org/10.1016/j.compscitech.2020.108259

IF: 9.1

2020-09-01

Composites Science and Technology

Abstract:<p>The continuous glass fibers (CGFs) reinforced thermoplastic composites play a crucial role in many applications such as automobile industry and aeronautic industry. However, there are two problems, one is how to regulate the degree of impregnation (<em>M</em>) and fracture rate of fiber bundle (<em>P</em>), and another is how to improve the interfacial properties. In this work, the different impregnated rollers configurations were designed to obtain appropriate <em>M</em> and <em>P</em> value, and the polyethylenimine (PEI) functionalized carboxylic carbon nanotubes (PEI-CNT) were grafted to the CGFs (PEI-CNT-CGFs) surface through dipping method, which is beneficial to the interfacial properties between CGFs and polypropylene (PP). Both theoretical and experimental results indicated that optimal configuration (F) could achieve ultrahigh degree of impregnation of 99.37% at relatively low fracture rate (3.58%) of fiber bundle, so that the tensile strength was improved dramatically (from 329.3 MPa to 461.8 MPa). Furthermore, the PP/PEI-CNT-CGFs composite manufactured in F configuration showed higher tensile strength (486.3 MPa) due to the better interfacial adhesion, it was an obvious consequence from the SEM images of fractured surface in PP/PEI-CNT-CGFs. This study provides a strategy to obtain ultrahigh performance of CGFs reinforced PP composite by improving degree of impregnation as much as possible with limited fiber breakage, and enhancing interfacial adhesion. It is hugely significant to guide the production of CGFs reinforced thermoplastic prepreg composites.</p>

materials science, composites

What problem does this paper attempt to address?

The paper primarily aims to address the issues encountered during the preparation of continuous glass fiber reinforced polypropylene prepreg composites (CGFs reinforced polypropylene prepreg composites). Specifically, the research focuses on two key issues:

1. **How to adjust the impregnation degree (M) and fiber bundle breakage rate (P)**: This is one of the key challenges to overcome during the melt impregnation process. Excessive melt viscosity and poor wettability hinder the polypropylene resin from fully penetrating the tiny gaps within the continuous glass fiber (CGFs) bundles.

2. **How to improve interfacial performance**: That is, enhancing the interaction between continuous glass fibers and the polypropylene matrix, which is crucial for obtaining high-performance composites.

To address the above issues, the authors designed a series of different impregnation roller configurations to achieve appropriate impregnation degrees and fiber breakage rates. They also grafted polyethyleneimine-functionalized carboxylic acid-functionalized carbon nanotubes (PEI-CNT) onto the surface of continuous glass fibers through an impregnation method to improve the interfacial properties between the fibers and polypropylene. The research results show that the optimal configuration (F configuration) can achieve ultra-high impregnation degree (99.37%) at a relatively low fiber breakage rate (3.58%), thereby significantly improving the tensile strength of the composites (from 329.3 MPa to 461.8 MPa). Furthermore, the polypropylene/PEI-CNT-CGFs composites manufactured under the F configuration exhibited higher tensile strength (486.3 MPa) due to better interfacial bonding.

In summary, this study provides a strategy to obtain high-performance continuous glass fiber reinforced polypropylene composites by maximizing the impregnation degree while limiting fiber breakage and enhancing interfacial bonding. This achievement is of great significance for guiding the production of continuous fiber reinforced thermoplastic prepreg composites.