Abstract:Electro-reduction of O2 to generate H2O2 is an attractive alternative to the current anthraquinone process and quietly necessary for the chemical industries and environmental remediation. It is general that sufficient porous structure contributes to expose more catalytic active sites and shorten diffusion paths for the heterogeneous catalysis of O2. In this work, initially, the Fe3O4 nanoparticles embedded graphite felt (Fe3O4@GF) is prepared through a mild hydrothermal following with thermal reduction method. This special combination not only provides iron source for the electro-Fenton reaction, but also supplies rich active sites from the Fe3O4 embedded structure with abundant cracks, which are beneficial to increase the reaction rate. Compared with raw graphite felt (RGF), the fresh Fe3O4@GF exhibits superior pollutant degradation kinetics with more than 400% increase and approximately 37.8% improvement to the removal of total organic carbon. 98% decolorization of rhodamine B (RhB) can be achieved in just 5 minutes, and quickly complete 100% removal of RhB in the next few seconds. As the electro-Fenton reaction progresses, Fe3O4 dissolves in the electrolyte, leaving porous structure on the surface of the GF to form a porous GF (PGF), and the rapid radical reaction activates GF surface. Both the chemical etching of Fe3O4 and the electro-Fenton process can further increase the specific surface area, defects and actives sites of the electrode. As expected, the active PGF exhibits favorable performance of H2O2 production among in pH=1 (320.0±36.5 mg L-1), 3 (301.9±13.2 mg L-1) and 7 (320.4±21.2 mg L-1) electrolyte. The degradation performance of PGF does not significantly decay even after 20 times repeated use, indicating the good structural stability and long-term durability. The superiority of the in-situ Fe source and fast reaction kinetics for electro-Fenton of Fe3O4@GF is confirmed, and this holey-engineered strategy also provides the possibility to achieve swift water purification and open up a new way for developing efficient carbon-based electrodes.

Synthesis of PbO x to graphite felt anodes to improve the electro-assisted catalytic wet air oxidation of oxygen species for efficient dye degradation

Synthesis of PbOx to Graphite Felt Anodes to Improve the Electro-Assisted Catalytic Wet Air Oxidation of Oxygen Species for Efficient Dye Degradation

Electrochemical Degradation of Antibiotic Enoxacin Using a Novel PbO2 Electrode with a Graphene Nanoplatelets Inter-Layer: Characteristics, Efficiency and Mechanism.

Preparation and characterization of PbO₂ electrode and its application in electro-catalytic degradation of o-aminophenol in aqueous solution assisted by CuO-Ce₂O₃/γ-Al₂O₃ catalyst.

Tuning the Morphology and Surface Structure of MnOx@GF Through Ce for High-Efficiency Degradation of Rhodamine B by Electro-Fenton

Electro-activation of O2 on MnO2/graphite felt for efficient oxidation of water contaminants under room condition

Room-temperature air oxidation of organic pollutants via electrocatalysis by nanoscaled Co-CoO on graphite felt anode

Efficient H2O2 electrogeneration at graphite felt modified via electrode polarity reversal: Utilization for organic pollutants degradation

Polydopamine/graphite sheet electrode for highly efficient electrocatalytic hydrogen peroxide generation and bisphenol A removal

Anodized graphite felt as an efficient cathode for in-situ hydrogen peroxide production and Electro-Fenton degradation of rhodamine B

Efficient degradation of rhodamine B using modified graphite felt gas diffusion electrode by electro-Fenton process

Enhancement of H2O2 yield and TOC removal in electro-peroxone process by electrochemically modified graphite felt: Performance, mechanism and stability

Electrochemical Pretreatment of Coal Gasification Wastewater with Bi-doped PbO2 Electrode: Preparation of Anode, Efficiency and Mechanism.

Molten salt synthesis of porous graphene-like carbons as peroxydisulfate catalyst for the efficient removal of rhodamine B dye

Ultrahigh yield of hydrogen peroxide on graphite felt cathode modified with electrochemically exfoliated graphene

Molecular-Level Tuning of Active Sites of the Carbonaceous Catalyst for Boosting Electrochemical H2O2 Production and Its Application in Electro-Fenton-like Degradation of Organics

Oxidative Modification of Graphite Felts for Efficient H2O2 Electrogeneration: Enhancement Mechanism and Long-Term Stability

Combined Electro-Catazone/electro-peroxone Process for Rapid and Effective Rhodamine B Degradation

Iron-modified granular sludge biochar-based catalysts for improved Rhodamine B degradation by activating peroxymonosulfate

Simultaneously Providing Iron Source towards Electro-Fenton Process and Enhancing Hydrogen Peroxide Production via a Fe3O4 Nanoparticles Embedded Graphite Felt Electrode.

Synergetic Degradation Of Rhodamine B At A Porous Znwo4 Film Electrode By Combined Electro-Oxidation And Photocatalysis