Abstract:Objectives: To design and prepare silk fibroin/hyaluronic acid composite hydrogel. Methods: The thiol modified silk fibroin and the double-bond modified hyaluronic acid were rapidly cured into gels through thiol-ene click polymerization under ultraviolet light condition. The grafting rate of modified silk fibroin and hyaluronic acid was characterized by 1H NMR spectroscopy; the gel point and the internal microstructure of hydrogels were characterized by rheological test and scanning electron microscopy; the mechanical properties were characterized by compression test; the swelling rate and degradation rate were determined by mass method. The hydrogel was co-cultured with the cells, the cytotoxicity was measured by the lactate dehydrogenase method, the cell adhesion was measured by the float count method, and the cell growth and differentiation on the surface of the gel were observed by scanning electron microscope and fluorescence microscope. Results: The functional group substitution degrees of modified silk fibroin and hyaluronic acid were 17.99% and 48.03%, respectively. The prepared silk fibroin/hyaluronic acid composite hydrogel had a gel point of 40-60 s and had a porous structure inside the gel. The compressive strength was as high as 450 kPa and it would not break after ten cycles. The water absorption capacity of the composite hydrogel was 4-10 times of its own weight. Degradation experiments showed that the hydrogel was biodegradable, and the degradation rate reached 28%-42% after 35 d. The cell biology experiments showed that the cytotoxicity of the composite gel was low, the cell adhesion was good, and the growth and differentiation of the cells on the surface of the gel were good. Conclusions: The photocurable silk fibroin/hyaluronic acid composite hydrogel can form a gel quickly, and has excellent mechanical properties, adjustable swelling rate and degradation degree, good biocompatibility, so it has promising application prospects in biomedicine.

Synthesis and Characterization of Photo-Cross-Linkable Silk Fibroin Methacryloyl Hydrogel for Biomedical Applications

Research Progress on Gelling Mechanism and Modification of Silk Fibroin Hydrogels

Preparation and Characterization of Photo-Cross-Linkable Methacrylated Silk Fibroin and Methacrylated Hyaluronic Acid Composite Hydrogels

Fabrication and characterization of porous tubular silk fibroin scaffolds.

Self‐Healing Silk Fibroin‐Based Hydrogel for Bone Regeneration: Dynamic Metal‐Ligand Self‐Assembly Approach

Investigation on the Structure and Mechanical Properties of Highly Tunable Elastomeric Silk Fibroin Hydrogels Cross-Linked by γ-Ray Radiation.

Investigation On The Structure And Mechanical Properties Of Highly Tunable Elastomeric Silk Fibroin Hydrogels Cross-Linked By Gamma-Ray Radiation

Fabrication of hydrogel scaffolds via photocrosslinking of methacrylated silk fibroin

Versatile Potential of Photo-Cross-Linkable Silk Fibroin: Roadmap from Chemical Processing Toward Regenerative Medicine and Biofabrication Applications

Superb Silk Hydrogels with High Adaptability, Bioactivity, and Versatility Enabled by Photo-Cross-Linking

Preparation of silk fibroin/hyaluronic acid composite hydrogel based on thiol-ene click chemistry

Preparation of silk fibroin/hyaluronic acid hydrogels with enhanced mechanical performance by a combination of physical and enzymatic crosslinking

Fabrication and characterization of silk microfiber-reinforced methacrylated gelatin hydrogel with turnable properties

Crosslinking strategies for silk fibroin hydrogels: promising biomedical materials

Structure and properties of protein-based fibrous hydrogels derived from silk fibroin and sodium alginate

Processing, mechanical properties and bio-applications of silk fibroin-based high-strength hydrogels

Sodium oleate induced rapid gelation of silk fibroin

Photocrosslinked Silk Fibroin Microgel Scaffolds for Biomedical Applications

Photocrosslinked Silk Fibroin Microgel Scaffolds for Biomedical Applications (Adv. Funct. Mater. 29/2024)

Dityrosine-inspired photocrosslinking technique for 3D printing of silk fibroin-based composite hydrogel scaffolds

Mild preparation of hyaluronic acid/silk fibroin sponges by modified crosslinking method