Abstract:Objectives: To design and prepare silk fibroin/hyaluronic acid composite hydrogel. Methods: The thiol modified silk fibroin and the double-bond modified hyaluronic acid were rapidly cured into gels through thiol-ene click polymerization under ultraviolet light condition. The grafting rate of modified silk fibroin and hyaluronic acid was characterized by 1H NMR spectroscopy; the gel point and the internal microstructure of hydrogels were characterized by rheological test and scanning electron microscopy; the mechanical properties were characterized by compression test; the swelling rate and degradation rate were determined by mass method. The hydrogel was co-cultured with the cells, the cytotoxicity was measured by the lactate dehydrogenase method, the cell adhesion was measured by the float count method, and the cell growth and differentiation on the surface of the gel were observed by scanning electron microscope and fluorescence microscope. Results: The functional group substitution degrees of modified silk fibroin and hyaluronic acid were 17.99% and 48.03%, respectively. The prepared silk fibroin/hyaluronic acid composite hydrogel had a gel point of 40-60 s and had a porous structure inside the gel. The compressive strength was as high as 450 kPa and it would not break after ten cycles. The water absorption capacity of the composite hydrogel was 4-10 times of its own weight. Degradation experiments showed that the hydrogel was biodegradable, and the degradation rate reached 28%-42% after 35 d. The cell biology experiments showed that the cytotoxicity of the composite gel was low, the cell adhesion was good, and the growth and differentiation of the cells on the surface of the gel were good. Conclusions: The photocurable silk fibroin/hyaluronic acid composite hydrogel can form a gel quickly, and has excellent mechanical properties, adjustable swelling rate and degradation degree, good biocompatibility, so it has promising application prospects in biomedicine.

Superb Silk Hydrogels with High Adaptability, Bioactivity, and Versatility Enabled by Photo-Cross-Linking

Design of Multistimuli Responsive Hydrogels Using Integrated Modeling and Genetically Engineered Silk–Elastin‐Like Proteins

Research Progress on Gelling Mechanism and Modification of Silk Fibroin Hydrogels

Lyophilized Silk Sponges: A Versatile Biomaterial Platform for Soft Tissue Engineering

Engineering Natural and Recombinant Silks for Sustainable Biodevices

Robust Silk Protein Hydrogels Made by a Facile One-Step Method and Their Multiple Applications

Preparation of silk fibroin/hyaluronic acid hydrogels with enhanced mechanical performance by a combination of physical and enzymatic crosslinking

Physically Crosslinked Biocompatible Silk‐Fibroin‐Based Hydrogels with High Mechanical Performance

High‐Strength, Durable All‐Silk Fibroin Hydrogels with Versatile Processability Toward Multifunctional Applications

Silk fibroin hydrogels for biomedical applications

Processing, mechanical properties and bio-applications of silk fibroin-based high-strength hydrogels

Fabrication of Silk Hydrogel Scaffolds with Aligned Porous Structures and Tunable Mechanical Properties

Synthesis and Characterization of Photo-Cross-Linkable Silk Fibroin Methacryloyl Hydrogel for Biomedical Applications

Preparation of silk fibroin/hyaluronic acid composite hydrogel based on thiol-ene click chemistry

Mechanically Resilient, Injectable, and Bioadhesive Supramolecular Gelatin Hydrogels Crosslinked by Weak Host-Guest Interactions Assist Cell Infiltration and in Situ Tissue Regeneration

Versatile Potential of Photo-Cross-Linkable Silk Fibroin: Roadmap from Chemical Processing Toward Regenerative Medicine and Biofabrication Applications

Crosslinking strategies for silk fibroin hydrogels: promising biomedical materials

Robust Protein Hydrogels from Silkworm Silk

Fabrication and characterization of silk microfiber-reinforced methacrylated gelatin hydrogel with turnable properties

Progress in Hydrogels Based on Regenerated Silk Fibroin

Long-Lasting Thixotropic Natural Polymeric Hydrogel Based on Silk Nanofibrils.