Hot Deformation Behavior and Mechanism of Ti–6Al–4V–2Mo–2Fe Titanium Alloy With Satisfactory Hot Workability

Jie Shen,Zhihao Zhang,Jianxin Xie
DOI: https://doi.org/10.1007/s11661-023-07153-2
2023-09-02
Abstract:The high-temperature flow behavior, hot processing map, microstructure, and hot deformation mechanism of Ti–6Al–4V–2Mo–2Fe (Ti6422) designed by the authors and traditional Ti–6Al–4V (TC4) alloys were compared. The results showed that the peak flow stress of Ti6422 alloy was lower than that of TC4 compressed at the strain rates of 0.001 to 10 s −1 and temperatures of 800 °C to 900 °C. The maximum difference was approximately 120 MPa at 800 °C and 0.01 s −1 . The reduced high-temperature flow stress of Ti6422 alloy was primarily attributed to enhanced dynamic recrystallization and reduced dislocation density. Ti6422 alloy exhibited a smaller deformation instability region, wider hot processing window, lower hot deformation activation energy (352 KJ/mol), and higher strain rate sensitivity exponent (0.172) compared to TC4 alloy. During hot deformation, Ti6422 exhibited easier activation of the prismatic slip and pyramidal slip system with the main deformation mechanism being dislocation movement. In contrast, TC4 required the initiation of the twin mechanism in addition to the dislocation mechanism.
What problem does this paper attempt to address?