Abstract:Nickel-based single crystal superalloys, as engine blade materials, are prone to fatigue damage due to repeated startups and shutdowns. Therefore, monitoring and quantitatively estimating fatigue cracks are essential for engineering structures to ensure safety. In this study, we proposed a method for fatigue crack segmentation and damage prediction based on deep learning and in-situ high-temperature scanning electron microscopy (SEM). Sequential SEM images describing the crack initiation and propagation under near-service conditions were obtained by conducting in-situ high-temperature fatigue experiments. A fatigue crack dataset with high-quality was thus constructed for further dynamic and real-time crack segmentation and damage assessment. Deep learning-based models were used to segment cracks and predict damage behavior (i.e., crack area, length, width, and stress intensity factors) at future based on prior damage information. The short-term and long-term damage prediction capability were validated by comparing model performance when predicting damage at different future time points. Additionally, we compared the model performance when predicting damage at specific time point based on varying lengths of input sequence. Results demonstrated that the model could segment cracks and scales with different sizes accurately. The model performed well in short-term damage prediction. The long-term predictive performance showed decrease than that of short-term, which could be improved by feeding long length of input sequence. The proposed approach demonstrates the feasibility and effectiveness of deep learning-based crack segmentation and damage prediction, which facilitates the move toward real-time analysis and rapid diagnosis of material damage in the future.

A comparative study of creep-fatigue life prediction for complex geometrical specimens using supervised machine learning

A Robust Life Prediction Model for a Range of Materials under Creep-Fatigue Interaction Loading Conditions

Machine Learning-Assisted Probabilistic Creep Life Assessment for High-Temperature Superheater Outlet Header Considering Material Uncertainty

Composition, heat treatment, microstructure and loading condition based machine learning prediction of creep life of superalloys

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

A deep learning based life prediction method for components under creep, fatigue and creep-fatigue conditions

Predicting creep rupture life of Ni-based single crystal superalloys using divide-and-conquer approach based machine learning

A novel machine learning method for multiaxial fatigue life prediction: Improved adaptive neuro-fuzzy inference system

A physics-informed neural network for creep-fatigue life prediction of components at elevated temperatures

Machine learning assisted probabilistic creep-fatigue damage assessment

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

A novel method of multiaxial fatigue life prediction based on deep learning

A unified creep and fatigue life prediction approach for 316 austenitic stainless steel using machine and deep learning

Novel models for fatigue life prediction under wideband random loads based on machine learning

A Method for Predicting the Creep Rupture Life of Small-Sample Materials Based on Parametric Models and Machine Learning Models

Fitting and Prediction for Crack Propagation Rate Based on Machine Learning Optimal Algorithm

Creep strain prediction in power plant material via ANN modelling of nonlinear ultrasonic test results

Machine learning‐based genetic feature identification and fatigue life prediction

Prediction of fatigue crack propagation lives based on machine learning and data-driven approach

Study of fatigue crack propagation on modified CT specimens under variable amplitude loadings using machine learning