Abstract:Nickel-based single crystal superalloys, as engine blade materials, are prone to fatigue damage due to repeated startups and shutdowns. Therefore, monitoring and quantitatively estimating fatigue cracks are essential for engineering structures to ensure safety. In this study, we proposed a method for fatigue crack segmentation and damage prediction based on deep learning and in-situ high-temperature scanning electron microscopy (SEM). Sequential SEM images describing the crack initiation and propagation under near-service conditions were obtained by conducting in-situ high-temperature fatigue experiments. A fatigue crack dataset with high-quality was thus constructed for further dynamic and real-time crack segmentation and damage assessment. Deep learning-based models were used to segment cracks and predict damage behavior (i.e., crack area, length, width, and stress intensity factors) at future based on prior damage information. The short-term and long-term damage prediction capability were validated by comparing model performance when predicting damage at different future time points. Additionally, we compared the model performance when predicting damage at specific time point based on varying lengths of input sequence. Results demonstrated that the model could segment cracks and scales with different sizes accurately. The model performed well in short-term damage prediction. The long-term predictive performance showed decrease than that of short-term, which could be improved by feeding long length of input sequence. The proposed approach demonstrates the feasibility and effectiveness of deep learning-based crack segmentation and damage prediction, which facilitates the move toward real-time analysis and rapid diagnosis of material damage in the future.

A unified creep and fatigue life prediction approach for 316 austenitic stainless steel using machine and deep learning

Ultra-low Cycle Fatigue Life Prediction of Stainless Steel Based on Transfer Learning Guided Artificial Neural Network

A deep learning based life prediction method for components under creep, fatigue and creep-fatigue conditions

A deep learning-based method for predicting the low-cycle fatigue life of austenitic stainless steel

A Robust Life Prediction Model for a Range of Materials under Creep-Fatigue Interaction Loading Conditions

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

A physics‐informed neural network for creep life prediction of austenitic stainless steels in air and liquid sodium

A cGAN-based fatigue life prediction of 316 austenitic stainless steel in high-temperature and high-pressure water environments

Prediction of 316 stainless steel low-cycle fatigue life based on machine learning

Analysis of High-Cycle Fatigue Life Prediction of 304 Stainless Steel Based on Deep Learning

Assessment of prior fatigue damage and a new approach to predict remanent creep rupture of P92 steel

Machine learning approach for predicting and understanding fatigue crack growth rate of austenitic stainless steels in high-temperature water environments

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

A physics-informed neural network for creep-fatigue life prediction of components at elevated temperatures

Composition, heat treatment, microstructure and loading condition based machine learning prediction of creep life of superalloys

New Creep Crack Growth Prediction Model for the Life Assessment of Stainless-Steel Material Using Computational Modeling

Development of damage evaluation system for heat resistant steel for creep and creep fatigue based on deep learning of grain shape and strain information by EBSD observation

Machine Learning-Assisted Probabilistic Creep Life Assessment for High-Temperature Superheater Outlet Header Considering Material Uncertainty

A Generalized Hysteresis Energy Method for Fatigue and Creep-Fatigue Life Prediction of 316L(N)

An explainable machine learning model for superalloys creep life prediction coupling with physical metallurgy models and CALPHAD

Data-Enhanced Low-Cycle Fatigue Life Prediction Model Based on Nickel-Based Superalloys