Abstract:Poly(lactic acid) (PLA), as a kind of aliphatic polyester derived from biomass with excellent mechanical strength, biocompatibility and biodegradability, is a kind of green polymers with promising potential application. However, the application of PLA as a commodity polyester has been restricted dramatically because of its brittleness and flammability nature. It is still a great challenge to improve flame retardancy and toughness of PLA simultaneously by a simple blending method. In this work, copolymer ionomer (PCLA-PIU) was prepared by chain extension copolymerization of hydroxyl terminated poly(e-caprolactone) (PCL), PLA prepolymer and phenylhypophosphate, and then incorporated with ammonium polyphosphate (APP) for synergistic modification of PLA. The ionomer can act as a compatibilizer to enhance the dispersion of APP in PLA matrix because of its PLA segments and phenylhypophosphate groups. The SEM observation shows that the APP particles dispersed in PLA/PCLA-PIU/APP composite has significantly smaller size and uniform dispersity, compared to the PLA/APP20. The phenyl hypophosphate groups in the ionomer also has an excellent synergistic effect with APP for improving the flame-retardance of PLA. The flame-retardant properties and mechanism of the PLA and its composites were investigated by LOI, UL-94, Cone calorimeter test, SEM, EDS, Raman spectroscopy, etc. Compared with neat PLA and PLA/APP, the composite PLA/PCLA-PIU10/APP10 containing 10 wt% of PCLAP-IU and 10 wt% of APP10 achieves the V-0 rating in UL-94 burning test with limiting oxygen index (LOI) as high as 27.6%. The heat release rate and total heat release of PLA/PCLA-PIU10/APP10 are also reduced significantly to 254.9 kW/m(2) and 55.8 MJ/m(2), respectively. SEM and Raman analysis for char residues after Cone calorimeter test suggest PCLA-PIU and APP had synergistic effect on promoting charring of PLA, which result in compact char residue with high graphitization degree, therefore effectively improving the flame-retardant efficiency. Moreover, the toughness of PLA is improved effectively by the flexible PCL segments of ionomers, resulting in a PLA/PCLA-PIU/APP composite with improved flame retardancy and toughness simultaneously. The mechanical properties test results show that the toughness of the modified PLA (10.3 kJ/m(2) of PLA/PCLA-PIU10/APP10) is significantly improved compared to those of neat PLA (3.7 kJ/m(2)) and PLA/APP20 (2.5 kJ/m(2)).

Enhancement of mechanical and flame‐retardant properties of PLA composites through the combined action of flexible chain segments and hydrogen bonding interactions

Improved properties of PLA biocomposites toughened with bamboo cellulose nanowhiskers through silane modification

Preparation of Polylactide Composite with Excellent Flame Retardance and Improved Mechanical Properties

Enhanced Flame Retardancy and Mechanical Properties of Poly (lactic Acid) Composites Via Piperazine Pyrophosphate and Nanoscale Cerium Dioxide Synergistic Flame Retarding and Uniaxial Pre-Stretching

Preparation and Mechanism of Toughened and Flame-Retardant Bio-Based Polylactic Acid Composites

Improving the toughness and flame retardancy of poly (lactic acid) with phosphorus‐containing core‐shell particles

Preparation of super toughened flame-retardant polylactic acid with an in situ hyperbranched structure by reactive blending with a phosphorus-containing copolyester and hexamethylene glycidyl cyclotriphosphazene

Tough and Flame-Retardant Poly(lactic Acid) Composites Prepared Via Reactive Blending with Biobased Ammonium Phytate and in Situ Formed Crosslinked Polyurethane

Synchronously Enhanced Flame Retardancy and Mechanical Properties of Polylactic Acid Via In-Situ Assembly of Polyphosphazene Nanoparticles on Ammonium Polyphosphate

Molecularly engineered polyphosphazene-derived for advanced polylactide biocomposites with robust toughness, flame retardancy, and UV resistance

Enhancement of Flame Retardancy and Mechanical Properties of Polylactic Acid with a Biodegradable Fire-Retardant Filler System Based on Bamboo Charcoal

Flame Retardant and Toughening Modification of Poly(lactic acid) with Phenylhypophosphate Ionomer/Ammonium Polyphosphate

Achieving simultaneously toughening and flame-retardant modification of poly(lactic acid) by in-situ formed cross-linked polyurethane and reactive blending with ammonium polyphosphate

Construction of carbon-based flame retardant composite with reinforced and toughened property and its application in polylactic acid

Simultaneously Enhance Both the Flame Retardancy and Toughness of Polylactic Acid by the Cooperation of Intumescent Flame Retardant and Bio-Based Unsaturated Polyester

Fabrication of nickel–cobalt bimetallic hydroxide modified by chitosan and benzenephosphonic acid with high catalytic carbonization as a novel flame retardant for polylactic acid

Mechanically robust and flame-retardant poly(lactide)/poly(butylene adipate-co-terephthalate) composites based on carbon nanotubes and ammonium polyphosphate

A method for simultaneously improving the flame retardancy and toughness of PLA

Flame-retardant and UV-shielding poly (lactic acid) composites with preserved mechanical properties by incorporating cyclophosphazene derivative and phosphorus-modified lignin

Scalable Manufacturing Green Core–Shell Structure Flame Retardant, with Enhanced Mechanical and Flame-Retardant Performances of Polylactic Acid

A nimble strategy for enabling bioderived flame retardants with strikingly enhanced interfacial compatibility in poly (lactic acid) composites