The hot corrosion behavior in vanadate environment and thermal cycling behaviors of YTZ and 2GYTZ for thermal barrier coating applications

Jinshuang Wang,Luyao Chen,Linfeng Niu,Jiaojiao Yang,Mengfan Wang,Junbin Sun,Yongsheng Yu,Yinghui Wang,Bing Liu,Qiangshan Jing
DOI: https://doi.org/10.1016/j.surfcoat.2020.126499
IF: 4.865
2020-12-01
Surface and Coatings Technology
Abstract:<p>A preliminary examination was carried out for hot corrosion resistance to V<sub>2</sub>O<sub>5</sub> and thermal cycling behaviors of two alternative materials: zirconia co-doped with 16 mol% YO<sub>1.5</sub> + 16 mol% TaO<sub>2.5</sub> (YTZ) and zirconia co-doped with 14 mol% YO<sub>1.5</sub>+ 2 mol% GdO<sub>1.5</sub> + 16 mol% TaO<sub>2.5</sub> (2GYTZ). The compositions and microstructures of the samples were analyzed by X-ray diffraction (XRD), scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDS). Results showed ZrV<sub>2</sub>O<sub>7</sub> and YVO<sub>4</sub>/GdVO<sub>4</sub> were the main reaction products at 750 °C and 850 °C for 2 h, while YVO4 and m-ZrO<sub>2</sub> were detected as the main corrosion products at 850 °C for 10 h or rising temperature to 950 °C. With the depletion of V<sub>2</sub>O<sub>5</sub>, ZrV<sub>2</sub>O<sub>7</sub> disappeared and decomposed into m-ZrO<sub>2</sub> and V<sub>2</sub>O<sub>5</sub>. The hot corrosion mechanisms are similar for YTZ and 2GYTZ ceramics. However, the amount of m-ZrO<sub>2</sub> in the 2GYTZ was much more than that in the YTZ at the same corrosion conditions. The weaker bonds due to partial substitution of Y<sup>3+</sup> with larger size of Gd<sup>3+</sup> and the size misfit between Gd<sup>3+</sup> and Zr<sup>4+</sup> resulted in decreasing the anti-corrosion capability of 2GYTZ ceramic. The tetragonal phase was very stable for YTZ and 2GYTZ coatings during high temperature heat treatment. The thermal durability of the YTZ and 2GYTZ TBCs can be significantly improved by using the YSZ buffer layer. While the cycling lifetimes for 2GYTZ coating was much shorter than that of YTZ coating whether designed for single-ceramic-layer structure or double-ceramic-layer structure. Failure of the 2GYTZ coating mainly resulted from the thermal expansion mismatch stress, concentrated thermal stress introduced by the severe sintering and low fracture toughness.</p>
physics, applied,materials science, coatings & films
What problem does this paper attempt to address?